Copolyesters containing neopentyl glycol and 2,2,4,4-tetraalkyl 1,3-cyclobutanediol

ABSTRACT

There is provided a copolyester containing residues of neopentyl glycol, 2,2,4,4-tetraalkyl 1,3-cyclobutanediol such as 2,2,4,4-tetramethyl 1,3-cyclobutanediol, tin atoms, aluminum atoms, an alkali or alkaline earth metal atoms such as lithium atoms, optionally phosphorus atoms, and having an It.V. of at least 0.55 dL/g, and Tg of at least 90° C. Such higher It.V. copolyesters can now be made having high Tg, good thermal stability, and higher insertion of 2,2,4,4-tetraalkyl 1,3-cyclobutanediol.

1. FIELD OF THE INVENTION

The present invention relates to copolyesters containing residues ofneopentyl glycol and 2,2,4,4-tetramethyl-1,3-cyclobutanediol having highintrinsic viscosity and thermal stability.

2. BACKGROUND OF THE INVENTION

High molecular weight copolyesters containing both neopentyl glycol(NPG) and 2,2,4,4-tetramethyl 1,3-cyclobutanediol (TMCD) are difficultto prepare using conventional catalysts (e.g. titanium and/or tin) andpolymerization conditions. TMCD can increase the glass transitiontemperature (Tg) in copolyesters made from dimethyl terephthalate (DMT)

Producing an amorphous copolyester having a high Tg is desirable forcertain end use applications where the polymer must remain dimensionallystable under heat. While TMCD can raise the Tg of an amorphouscopolyester, it becomes difficult to insert TMCD residues into thebackbone of the copolyester in the melt phase polycondensation toproduce a polymer with high Tg. Using an excess of TMCD to incorporatethe desired amount of TMCD into the backbone of the copolyester resultsin increased costs for use of the excess TMCD.

However, a polyester made using only TMCD as the glycol has such a highmelt viscosity that it is difficult to make and process. Therefore,other glycol comonomers are used to lower the melt viscosity of thepolymer melt and to also improve other properties such as toughness. Oneglycol that has been used is 1,4-cyclohexanedimethanol (CHDM).Copolyesters made from DMT, CHDM and TMCD have had commercial success,but can suffer from decreased thermal stability due to degradationreactions with the CHDM component, meaning that the polymer losesmolecular weight during high temperature processing of the polymer inmelt extrusion. Furthermore, high processing temperatures during themanufacture of the polymer, especially in the final polymerizationreactor, also called the finisher, are desirable to produce polymersfrom the melt that have a high molecular weight, typically measured asthe polymer's intrinsic viscosity (It.V). However, a polymer with poorthermal stability at the finisher reaction temperatures makes itdifficult to adequately build the IV (0.55 dL/g or more) needed for manyend use applications.

Thus, there remains a need to develop a copolyester containing TMCD thathas a good balance of high Tg (at least 90° C.), good IV (0.55 dL/g ormore), has an acceptable level of TMCD incorporation into the backboneof the copolyester polymer, and has good thermal stability.

3. SUMMARY OF THE INVENTION

There is now provided an amorphous copolyester composition comprising:

-   -   a) residues of 2,2,4,4-tetraalkyl-1,3-cyclobutanediol (TACD);    -   b) residues of neopentyl glycol (NPG);    -   c) alkali metal atoms or alkaline earth metal atoms;    -   d) aluminum atoms;    -   e) tin atoms;    -   f) an IV of at least 0.55 dL/g; and    -   g) a Tg of at least 90° C.

There is now also provided a process for making a copolyestercomposition comprising:

-   -   a) polycondensing a copolyester melt, comprising residues of NPG        and residues of TACD, to an IV of at least 0.55 dL/g in the        presence of an alakali or alkaline earth metal catalyst, an        aluminum catalyst, and a tin catalyst to obtain a high IV        copolyester melt; and    -   b) converting the high IV copolyester melt into amorphous        copolyester particles having a Tg of a least 90° C.        There is also provided a process for making a copolyester        composition comprising:    -   a) polycondensing a copolyester melt, comprising residues of NPG        and residues of TACD and residues of a tin catalyst, to an IV of        at least 0.55 dL/g in at a temperature of at least 275° C.; and    -   b) converting the high IV copolyester melt into amorphous        copolyester particles having a Tg of a least 90° C. and which is        thermally stable defined as having an average molecular weight        (Mw) of 15,000 or greater measured by melting a dried sample        (dried at 80° C. for at least 24 hours) of copolyester in a        nitrogen atmosphere at 310° C. for 25 minutes and determining        its Mw molecular weight at that point by Gel Permeation        Chromatography (“GPC”).

4. DETAILED DESCRIPTION OF THE INVENTION

The present invention may be understood more readily by reference to thefollowing detailed description of the invention.

As used in the specification and the appended claims, the singular forms“a,” “an” and “the” include plural referents unless the context clearlydictates otherwise. For example, reference to processing or making a“polymer,” a “preform,” “article,” “container,” or “bottle” is intendedto include the processing or making of a plurality of polymers,preforms, articles, containers or bottles.

References to a composition containing “an” ingredient or “a” polymer isintended to include other ingredients or other polymers, respectively,in addition to the one named.

By “comprising” or “containing” or “having” is meant that at least thenamed compound, element, particle, or method step etc. must be presentin the composition or article or method, but does not exclude thepresence of other compounds, catalysts, materials, particles, methodsteps, etc., even if the other such compounds, material, particles,method steps etc. have the same function as what is named, unlessexpressly excluded in the claims.

It is also to be understood that the mention of one or more method stepsdoes not preclude the presence of additional method steps before orafter the combined recited steps or intervening method steps betweenthose steps expressly identified. Moreover, the lettering of processsteps is a convenient means for identifying discrete activities orsteps, and unless otherwise specified, recited process steps can bearranged in any sequence. Expressing a range includes all integers andfractions thereof within the range. Expressing a range also includes theend points of the range regardless of whether the range is referred to anumber “within” or “between” or “of” certain expressed numbers. Theranges stated in this disclosure and the claims are intended to includethe entire range specifically and not just the endpoint(s). For example,a range stated to be 0 to 10 is intended to disclose all whole numbersbetween 0 and 10 such as, for example 1, 2, 3, 4, etc., all fractionalnumbers between 0 and 10, for example 1.5, 2.3, 4.57, 6.1113, etc., andthe endpoints 0 and 10.

Also, a range associated with chemical substituant groups such as, forexample, “C₁ to C₅ hydrocarbons”, is intended to specifically includeand disclose C₁ and C₅ hydrocarbons as well as C₂, C₃, and C₄hydrocarbons.

Expressing a temperature or a temperature range in a process, or of areaction mixture, or of a melt or applied to a melt, or of a polymer orapplied to a polymer means in all cases that the limitation is satisfiedif either the applied temperature, the actual temperature of the melt orpolymer, or both are at a value within the specified range, continuouslyor intermittently.

The word “composition” means a single ingredient or polymer or multipleingredients or polymers. Each listed ingredient is present in thecomposition, and the composition may contain any number and types ofother unspecified ingredients or polymers. A composition does not implythat an ingredient in the composition is unbound or unreacted. Thecomposition may be solid or liquid. The stated ingredients in thecomposition may be bound, unbound, reacted, unreacted, and unlessotherwise specified, in any oxidation state.

By “atoms” as used in conjunction with a metal is meant the metal atomoccupying any oxidation state, any morphological state, any structuralstate, and any chemical state, whether as added to or as present in thepolymer or composition of matter.

The term “polyester”, as used herein, is intended to include“copolyesters” and is understood to mean a synthetic polymer prepared bythe polycondensation of one or more difunctional carboxylic acids andtwo more difunctional hydroxyl compounds. Typically the difunctionalcarboxylic acid is a dicarboxylic acid and the difunctional hydroxylcompound is a dihydric alcohol such as, for example, glycols and diols.

The term “residue”, as used herein, means any organic structureincorporated into a polymer through a polycondensation reactioninvolving the corresponding monomer. The term “repeating unit”, as usedherein, means an organic structure having a dicarboxylic acid residueand a diol residue bonded through a carbonyloxy group. Thus, thedicarboxylic acid residues may be derived from a dicarboxylic acidmonomer or its associated acid halides, esters, salts, anhydrides, ormixtures thereof. As used herein, therefore, the term dicarboxylic acidis intended to include dicarboxylic acids and any derivative of adicarboxylic acid, including its associated acid halides, esters,half-esters, salts, half-salts, anhydrides, mixed anhydrides, ormixtures thereof, useful in a polycondensation process with a diol tomake high molecular weight copolyester.

The copolyester polymer of this invention is any thermoplasticcopolyester polymer in any state (e.g. solid or molten), and in anyshape, each as the context in which the phrase is used dictates, andincludes the composition of matter resulting from the melt phase, or thecomposition of matter in a melt extrusion zone, or articles made fromthe copolyester, such as injection molded articles, injection blowmolded articles, injection stretch blow molded articles, extruded film,extruded sheet, extrusion blow molded articles, and fibers.

The copolyester polymer is any thermoplastic copolyester polymer.Copolyester thermoplastic polymers of the invention are distinguishablefrom liquid crystal polymers and thermosetting polymers in thatthermoplastic polymers have no appreciable ordered structure while inthe liquid (melt) phase, they can be remelted and reshaped into a moldedarticle, and liquid crystal polymers and thermosetting polymers areunsuitable for the intended applications such as packaging or stretchingin a mold to make a container.

The copolyester polymer is desirably a random polymer such that themonomer units in the polymer chain are randomly arranged rather thanarranged in an ordered block fashion.

The term “melt phase polymerization” is a broad umbrella term referringto a stream undergoing reaction at any point in the melt phase formaking a copolyester polymer, and includes the composition in the firstesterification vessel and anywhere in the esterification phase eventhough the viscosity of the stream at this stage is typically notmeasurable or meaningful, and also includes the stream in thepolycondensation phase including the prepolymer and finishing phases,in-between each phase, and less than the point where the melt issolidified, and excludes a copolyester polymer undergoing an increase inmolecular weight in the solid state.

The copolyesters of this invention can be amorphous or semi-crystallinedepending on the type and amounts of monomers used. In one aspect,certain polyesters useful in the invention can have substantiallyamorphous morphology, meaning that the polyesters comprise substantiallyun-ordered regions of polymer. Amorphous copolyesters generally do nothave melting points.

The “bulk” of copolyester particles is defined as an accumulation ofparticles which together weigh at least 500 kg. A bulk having a definedcharacteristic can be determined by taking a random sampling of 10particles from the bulk for analysis. When it is said that a bulk ofcopolyester exhibit the characteristics expressed herein, it is meantthat a random sampling of 10 or more particles taken from the bulkexhibit an average of a defined characteristic determined by thesuitable analysis. As in any manufacturing process, it is possible toobtain anomalous particles which exhibit characteristics either insideor outside of those stated herein. The particles of the invention,however, exhibit the stated characteristics across a bulk, and thesecharacteristics can be measured by taking a random sampling of at leastten particles and determining the stated characteristics as an averageacross the ten particles. All ten particles may be measured together inone analysis, or each particle may be separately analyzed.

The bulk of copolyester polymer particles are desirably packaged into acontainer. Examples of suitable containers to hold the particles arestorage silos to hold the particles while they await shipment from onelocation to another. Another example of a container is a dryer hopperattached to an extruder or injection molding machine. Another example ofa container to hold the particles is a shipping container, such as aGaylord box, a crate, a railcar, a trailer that can be attached to atruck, a drum, a cargo hold on a ship, or any other suitable packageused to transport particles. Thus, there are provided containers withparticles which are finished and ready for shipment or in shipment to acustomer for converting the pellets to an article. The particles havebeen subjected by the particle manufacturer to all the processingconditions needed to produce a particle with characteristics acceptableto its customers who convert the pellets to articles. In the embodimentwhere the pellets may occupy a dryer hopper, the converter of pelletsplaces the bulk of the pellets into the dryer hopper and removesresidual moisture from the pellets to prevent excessive IV degradationduring melt processing.

In a preferred embodiment, the copolyester composition, or the bulk ofparticles, are not solid state polymerized. For example, there isprovided a bulk of particles in a container, most preferably a shippingcontainer, which have not been solid state polymerized, meaning theirmolecular weight has not been increased in the solid state by more than0.05 dL/g. Desirably, their molecular weight has not been increased inthe solid state by more than 0.02 dL/g, or even 0.01 dL/g.

The copolyester polymer particles are solid at 25° C. and 1 atmosphere.

The amorphous copolyester polymers, and the composition, of theinvention exhibit a glass transition temperature (abbreviated herein as“Tg”) of at least 90° C., as measured by well-known techniques such as,for example, differential scanning calorimetry (“DSC”) using a TA DSC2920 from TA Instruments at a scan rate of 20° C./min.

Desirably, the Tg of the amorphous copolyesters exhibit a Tg of at least92° C., or at least 94° C., or at least 96° C., or at least 98° C., orat least 100° C., or at least 102° C., or at least 104° C., or at least106° C., or at least 108° C., or at least 110° C., or at least 112° C.,or at least 144° C., or at least 116° C., or at least 118° C., or atleast 120, and up to 185° C., or up to less than 170° C., or up to 160°C., or less than 150° C., or less than 140° C., or less than 138° C., orless than 136° C., or less than 134° C., or less than 132° C., or lessthan 130° C., or less than 128° C., or less than 126° C., or less than124° C., or less than 122° C., or less than 120° C., or less than 118°C., or less than 116° C.

Exemplary ranges include a Tg in a range of 90 to 185 C; 90 to 180° C.;90 to 170° C.; 90 to 160° C.; 90 to 155° C.; 90 to 150° C.; 90 to 145°C.; 90 to 140° C.; 90 to 138° C.; 90 to 135° C.; 90 to 130° C.; 90 to125° C.; 90 to 120° C.; 90 to 115° C.; 90 to 110° C.; 90 to 105° C.; 90to 100° C.; 90 to 95° C.; 92 to 185° C.; 92 to 180° C.; 92 to 170° C.;92 to 160° C.; 92 to 155° C.; 92 to 150° C.; 92 to 145° C.; 92 to 140°C.; 92 to 138° C.; 92 to 136° C.; 92 to 134° C.; 92 to 132° C.; 92 to130° C.; 92 to 128° C.; 92 to 126° C.; 92 to 124° C.; 100 to 185° C.;100 to 160° C.; 100 to 150° C.; 100 to 145° C.; 100 to 140° C.; 100 to138° C.; 100 to 136° C.; 100 to 134° C.; 100 to 132° C.; 100 to 130° C.;100 to 128° C.; 100 to 126° C.; 105 to 185° C.; 105 to 160° C.; 105 to150° C.; 105 to 145° C.; 105 to 140° C.; 105 to 136° C.; 105 to 132° C.;105 to 128° C.; 110 to 185° C.; 110 to 160° C.; 110 to 150° C.; 110 to145° C.; 110 to 140° C.; 110 to 136° C.; 110 to 132° C.; and 110 to 128°C.

The IV referred to throughout means the intrinsic viscosity It.V. Wherethe IV refers to inherent viscosity it is referred to expressly as Ih.V.

The It.V. of the copolyester composition, and the copolyester polymers,is at least 0.55 dL/g. For example, the It.V. of the copolyesterparticles can be at least 0.58 dL/g, or at least 0.60 dL/g, or at least0.62 dL/g, or at least 0.64 dL/g, or at least 0.65 dL/g, or at least0.67 dL/g, or at least 0.69 dL/g, or at least 0.70 dL/g, or at least0.72 dL/g, or at least 0.74 dL/g, or at least 0.75 dL/g, or at least0.77 dL/g, or at least 0.79 dL/g, or at least 0.80 dL/g, or at least0.82 dL/g, and less than 0.85 dL/g, or less than 0.82 dL/g, or less than0.80 dL/g, or less than 0.78 dL/g, or less than 0.75 dL/g, or less than0.72 dL/g, or no more than 0.68 dL/g, or no more than 0.65 dL/g, or nomore than 0.63 dL/g, or no more than 0.60 dL/g, or no more than 0.58dL/g. Examples of ranges include 0.55 to 0.85 dL/g; 0.55 to 0.82 dL/g;0.55 to 0.80 dL/g; 0.55 to 0.75 dL/g; 0.55 to less than 0.75 dL/g; 0.55to 0.72 dL/g; 0.55 to 0.70 dL/g; 0.55 to less than 0.70 dL/g; 0.55 to0.68 dL/g; 0.55 to less than 0.68 dL/g; 0.55 to 0.67 dL/g; 0.55 to 0.65dL/g; 0.55 to 0.63 dL/g; 0.55 to 0.60 dL/g; 0.55 to 0.58 dL/g; 0.58 to0.85 dL/g; 0.58 to 0.80 dL/g; 0.58 to 0.75 dL/g; 0.58 to less than 0.75dL/g; 0.58 to 0.72 dL/g; 0.58 to 0.70 dL/g; 0.58 to less than 0.70 dL/g;0.58 to 0.68 dL/g; 0.58 to 0.65 dL/g; 0.60 to 0.85 dL/g; 0.60 to 0.80dL/g; 0.60 to 0.75 dL/g; 0.60 to less than 0.75 dL/g; 0.60 to 0.72 dL/g;0.60 to 0.70 dL/g; 0.60 to less than 0.70 dL/g; 0.60 to 0.68 dL/g; 0.60to less than 0.68 dL/g; 0.60 to 0.65 dL/g; 0.60 to 0.64 dL/g; 0.60 to0.68 dL/g; 0.64 to 0.85 dL/g; 0.64 to 0.80 dL/g; 0.64 to 0.75 dL/g; 0.64to less than 0.75 dL/g; 0.64 to 0.72 dL/g; 0.64 to 0.70 dL/g; 0.64 toless than 0.70 dL/g; 0.67 to 0.85 dL/g; 0.67 to 0.80 dL/g; 0.67 to 0.75dL/g; 0.67 to less than 0.75 dL/g; 0.67 to 0.72 dL/g; 0.69 dL/g to 0.85dL/g; 0.69 dL/g to 0.82 dL/g; 0.69 dL/g to 0.80 dL/g; 0.69 dL/g to 0.75dL/g; 0.69 dL/g to 0.72 dL/g; 0.72 dL/g to 0.85 dL/g; and 0.72 dL/g to0.82.

The intrinsic viscosity values described throughout this description areset forth in dL/g units as calculated from the inherent viscositymeasured at 25° C. in 60/40 wt/wt phenol/tetrachloroethane at aconcentration of 0.25 g/50 mL. We measure intrinsic viscosity accordingto ASTM D4603, with the exception that we prepare and measure thesolution at 25° C. instead of 30° C.

The inherent viscosity (Ih.V.) of the copolyester composition, and thecopolyester polymers, is at least 0.50 dL/g. For example, the Ih.V. ofthe copolyester particles can be at least 0.50 dL/g, or at least 0.53dL/g, or at least 0.55 dL/g, or at least 0.57 dL/g, or at least 0.60dL/g, or at least 0.62 dL/g, or at least 0.64 dL/g, or at least 0.65dL/g, or at least 0.67 dL/g, or at least 0.69 dL/g, or at least 0.70dL/g, or at least 0.72 dL/g, or at least 0.74 dL/g; and up to 0.83 dL/g,or less than 0.82 dL/g, or less than 0.80 dL/g, or less than 0.78 dL/g,or less than 0.75 dL/g, or less than 0.72 dL/g. Examples of rangesinclude 0.50 to 0.83 dL/g; 0.50 to 0.82 dL/g; 0.50 to 0.80 dL/g; 0.50 to0.75 dL/g; 0.50 to less than 0.75 dL/g; 0.50 to 0.72 dL/g; 0.50 to 0.70dL/g; 0.50 to less than 0.70 dL/g; 0.50 to 0.68 dL/g; 0.50 to less than0.68 dL/g; 0.50 to 0.67 dL/g; 0.50 to 0.65 dL/g; 0.58 to 0.83 dL/g; 0.58to 0.80 dL/g; 0.58 to 0.75 dL/g; 0.58 to less than 0.75 dL/g; 0.58 to0.72 dL/g; 0.58 to 0.70 dL/g; 0.58 to less than 0.70 dL/g; 0.58 to 0.68dL/g; 0.58 to less than 0.68 dL/g; 0.58 to 0.65 dL/g; 0.60 to 0.83 dL/g;0.60 to 0.80 dL/g; 0.60 to 0.75 dL/g; 0.60 to less than 0.75 dL/g; 0.60to 0.72 dL/g; 0.60 to 0.70 dL/g; 0.60 to less than 0.70 dL/g; 0.60 to0.68 dL/g; 0.60 to less than 0.68 dL/g; 0.60 to 0.65 dL/g; 0.60 to 0.64dL/g; 0.60 to 0.68 dL/g; 0.64 to 0.83 dL/g; 0.64 to 0.80 dL/g; 0.64 to0.75 dL/g; 0.64 to less than 0.75 dL/g; 0.64 to 0.72 dL/g; 0.64 to 0.70dL/g; 0.64 to less than 0.70 dL/g; 0.67 to 0.83 dL/g; 0.67 to 0.80 dL/g;0.67 to 0.75 dL/g; 0.67 to less than 0.75 dL/g; 0.67 to 0.72 dL/g; 0.69dL/g to 0.83 dL/g; 0.69 dL/g to 0.82 dL/g; 0.69 dL/g to 0.80 dL/g; 0.69dL/g to 0.75 dL/g; 0.69 dL/g to 0.72 dL/g; 0.72 dL/g to 0.83 dL/g; and0.72 dL/g to 0.82 dL/g, all in Ih.V units.

The amorphous copolyester polymer of the invention desirably containsalkylene terephthalate repeat units in the polymer chain. More desirableare copolyester polymers which comprise the residues of:

-   -   (a) an acid component comprising at least 80 mole % of the        residues of terephthalic acid, or desirably residues of the        derivates of terephthalic acid; and    -   (b) a hydroxyl component comprising at least 80 mole % of the        residues of NPG and TACD,        based on 100 mole percent of acid component residues and 100        mole percent of hydroxyl component residues in the copolyester        polymer.

The amorphous copolyesters can be made by reacting NPG and TACD with aC₁-C₄ dialkyl ester of terephthalic acid to produce an ester monomerand/or oligomers, which are then polycondensed to produce thecopolyester. More than one compound containing carboxylic acid group(s)or derivative(s) thereof can be reacted during the process. All thecompounds that enter the process containing carboxylic acid group(s) orderivative(s) thereof that become part of said copolyester productcomprise the “acid component.” The “residues” of compound(s) containingcarboxylic acid group(s) or derivative(s) thereof refers to the portionof said compound(s) which remains in the said copolyester product afterall the compounds are condensed and polycondensed to form copolyesterpolymer chains of varying length.

More than one compound containing hydroxyl group(s) or derivativesthereof can become part of the copolyester polymer product(s). All thecompounds that enter the process containing hydroxyl group(s) orderivatives thereof that become part of said copolyester product(s)comprise the hydroxyl component. The residues of hydroxyl functionalcompound(s) or derivatives thereof that become part of said copolyesterproduct refers to the portion of said compound(s) which remains in saidcopolyester product after said compounds are is condensed with acompound(s) containing carboxylic acid group(s) or derivative(s) thereofand further polycondensed to form copolyester polymer chains of varyinglength.

The mole % of the hydroxyl residues and carboxylic acid residues in theproduct(s) can be determined by proton NMR or gas chromatography.

Desirably, the copolyester polymer comprises:

-   -   (a) an acid component comprising at least 80 mole %, or at least        85 mole %, or at least 90 mole %, or at least 92 mole %, or at        least 96 mole % of terephthalic acid or desirably the residues        of a C₁-C₄ dialkyl ester of terephthalic acid, or in any event        at least 85 mole %, or at least 90 mole %, or at least 92 mole        %, or at least 96 mole % terephthalate units which includes the        —C(O)O— groups bonded to the aromatic ring; and    -   (b) a hydroxyl component comprising at least 85 mole %, or at        least 90 mole %, or at least 92 mole %, or at least 96 mole % of        the residues of TACD and NPG;        based on 100 mole percent of the acid component residues and 100        mole percent of the hydroxyl component residues in the        copolyester polymer.

The reaction of the acid component with the hydroxyl component duringthe preparation of the copolyester polymer is not restricted to thestated mole percentages since one may add an excess of the hydroxylcomponent during the manufacturing. The copolyester polymer made by thereaction will, however, contain the stated amounts of acid component andhydroxyl component.

Derivates of terephthalic acid include C₁-C₄ dialkylterephthalates suchas dimethylterephthalate. Desirably, the stated amount of the acidcomponent is the residue of the C₁-C₄ dialkyl ester of terephthalicacid, or dimethylterephthalate.

In addition to terephthalic acid and C₁-C₄ dialkyl ester of terephthalicacids, TACD, and NPG, other acid components and hydroxyl components canbe used as modifiers so long at the Tg of the polymer is maintained at alevel of at least 90° C.

Examples of acid modifiers include aromatic dicarboxylic acidspreferably having 8 to 14 carbon atoms, aliphatic dicarboxylic acidspreferably having 4 to 12 carbon atoms, or cycloaliphatic dicarboxylicacids preferably having 8 to 12 carbon atoms. More specific examples ofmodifier dicarboxylic acids useful as an acid component(s) are phthalicacid, isophthalic acid, naphthalene-2,6-dicarboxylic acid,cyclohexane-1,4-dicarboxylic acid, cyclohexanediacetic acid,diphenyl-4,4′-dicarboxylic acid, succinic acid, glutaric acid, subericacid, adipic acid, azelaic acid, sebacic acid, dimer acid,sulfoisophthalic acid, fumaric acid, maleic acid, itaconic acid,1,3-cyclohexanedicarboxylic acid, diglycolic acid,2,5-norbornanedicarboxyclic acid, diphenic acid, 4,4′-oxydibenzoic acid,4,4′-sulfonyldibenzoic acid, mixtures thereof, and the like. It shouldbe understood that use of the corresponding acid anhydrides, esters, andacid chlorides of these acids is included in the term “carboxylic acid”.It is also possible for tricarboxyl compounds and compounds with ahigher number of carboxylic acid groups to modify the copolyester.

In addition to a hydroxyl component comprising NPG and TACD, thehydroxyl component of the present copolyester may include modifiers.Hydroxyl modifiers are any hydroxyl bearing compound other than NPG andTACD. Hydroxyl modifiers including mono-ols, diols, or compounds with ahigher number of hydroxyl groups as branching monomers. Examples ofmodifier hydroxyl compounds include cycloaliphatic diols preferablyhaving 6 to 20 carbon atoms and/or aliphatic diols preferably having 2to 20 carbon atoms. More specific examples of such diols includeethylene glycol, diethylene glycol; triethylene glycol;1,2-cyclohexanedimethanol; 1,3-cyclohexanedimethanol;1,4-cyclohexanedimethanol; 1,2-propanediol; 1,3-propanediol;1,4-butanediol; 1,5-pentanediol; 1,6-hexanediol;3-methyl-2,4-pentanediol; 2-methyl-1,4-pentanediol;2,2,4-trimethylpentane-1,3-diol; 2,5-ethylhexane-1,3-diol;2,2-diethyl-1,3-propanediol; 1,3-hexanediol;1,4-di-(hydroxyethoxy)-benzene; 2,2-bis-(4-hydroxycyclohexyl)-propane;2,4-dihydroxy-1,1,3,3-tetramethyl-cyclobutane;2,2-bis-(3-hydroxyethoxyphenyl)-propane;2,2-bis-(4-hydroxypropoxyphenyl)-propane;2-butyl-2-ethyl-1,3-propanediol, 2-ethyl-2-isobutyl-1,3-propanediol,2,2,4,4-tetramethyl-1,6-hexanediol, 1,10-decanediol,1,4-benzenedimethanol, hydrogenated bisphenol A, isosorbide, propyleneglycol, dipropylene glycol, polytetramethylene glycol, tetraethyleneglycol, polyethylene glycol, and higher functional hydroxyl compoundswhich can be used as branching compounds including 1,1,1-trimethylolpropane, 1,1,1-trimethylolethane, glycerin, pentaerythritol, erythritol,threitol, dipentaerythritol, sorbitol, mixtures thereof, and the like.

One example of modifiers include isophthalic acid or naphthalenedicarboxylic acid added as acid modifiers, and cyclohexanedimethanol,ethylene glycol, or diethylene glycol added as hydroxyl modifiers.

The hydroxyl bearing modifiers, other than NPG and TACD, can be added inamount of less than 40 mole %, or less than 20 mole %, or less than 10mole %, or less than 8 mole %, or less than 5 mole %, or less than 3mole %, or less than 2 mole %, or less than 1 mole %, or less than 1mole %, or less than 0.5 mole %, or less than 0.25 mole %, and desirablynot added at all, based on the 100 mole percent of their respectivecomponent, acid or hydroxyl, in the polymer. The hydroxyl bearingmodifiers, other than NPG and TACD, are also desirably present in thepolymer in amounts of less than 20 mole %, or less than 10 mole %, orless than 5 mole %, or less than 4 mole %, or less than 2 mole %, orless than 1 mole %, or less than 0.5 mole %, based on the moles of allresidues in the copolyester (which by definition includes the residuesof the hydroxyl and acid component).

Desirably, the amount of all moieties present in the copolyester otherthan terephthalate, NGP, and TACD moieties, including both those due tomodifiers added and those formed in situ during the melt phasepolymerization, is less than 12 mole %, or not more than 10 mole %, ornot more than 8 mole %, or not more than 6 mole %, or not more than orless than 5 mole %, or not more than 5 mole percent, or not more than 4mol %, or not more than 2 mole %, or not more than 1 mole %, or not morethan less than 0.5 mole %, or not more than or less than 0.25 mole %, ornot more than or less than 0.1 mole %, or 0 mole %, based on the molesof all residues in the copolyester.

Desirably, the copolyester of the invention includes less than 5 mole %ethylene glycol residues, or less than 4 mole %, or less than 3 mole %,or less than 2 mole %, or less than 1 mole % based on the moles of allresidues in the copolyester. Desirably, no ethylene glycol is addedunless it is added as a carrier for a catalyst metal compound.Alternatively, no ethylene glycol is added.

The polyesters of the invention can comprise at least one chainextender. Suitable chain extenders include, but are not limited to,multifunctional (including, but not limited to, bifunctional)isocyanates, multifunctional epoxides, including for example, epoxylatednovolacs, and phenoxy resins. In certain embodiments, chain extendersmay be added at the end of the polymerization process or after thepolymerization process. If added after the polymerization process, chainextenders can be incorporated by compounding or by addition duringconversion processes such as injection molding or extrusion. The amountof chain extender used can vary depending on the specific monomercomposition used and the physical properties desired but is generallyabout 0.1 percent by weight to about 10 percent by weight, such as about0.1 to about 5 percent by weight, based on the total weight of thepolyester.

The copolyester composition may include blends of the amorphouscopolyesters along with other thermoplastic polymers such aspolycarbonate (PC) and polyamides. It is preferred that the copolyestercomposition should comprise a majority of the amorphous copolyesterpolymers, more preferably in an amount of at least 80 wt. %, or at least95 wt. %, and most preferably 100 wt. %, based on the weight of allthermoplastic polymers (excluding fillers, inorganic compounds orparticles, fibers, impact modifiers, or other polymers which may form adiscontinuous phase). It is also preferred that the copolyester polymersdo not contain any fillers, fibers, or impact modifiers or otherpolymers which form a discontinuous phase.

Desirably, the copolyester composition contains less than 60 wt %, orless than 40 wt %, or less than 20 wt. %, or less than 10 wt. %, or lessthan 5 wt. %, or no post-consumer recycled copolyester polymer (“PCR”)present in the composition, based on the total weight of all copolyesterpolymers. In another embodiment, the composition contains PCR in anamount of greater than zero and less than 60 wt. %, or less than 40 wt.%, or less than 20 wt %, or less than 10 wt. %, based on the totalweight of all copolyester polymers.

The copolyester composition comprises residues of TACD, and the processof the invention includes reacting TACD with the acid component to makea copolyester. It is desirable to use TACD. The TACD compositionincreases the Tg of the polymer.

The composition comprising TACD contains at least a2,2,4,4-tetraalkylcyclobutane-1,3-diol compound. Such a compound can berepresented by the general structure:

wherein R₁, R₂, R₃, and R₄ each independently represent an alkylradical, for example, a lower alkyl radical having 1 to 8 carbon atoms.The alkyl radicals may be linear, branched, or a combination of linearand branched alkyl radicals. Desirably, at least one of R₁, R₂, R₃, andR₄ is a methyl group, and preferably each of R₁, R₂, R₃, and R₄ is amethyl group.

The method for the manufacture of 2,2,4,4-tetraalkylcyclobutane-1,3-diolis not limited and any conventional or method known at any time can beused. One known method is the hydrogenation reaction of2,2,4,4-tetraalkylcyclobutane-1,3-dione to produce a2,2,4,4-tetraalkylcyclobutane-1,3-diol as shown below:

The 2,2,4,4-tetraalkylcyclobutane-1,3-dione, for example,2,2,4,4-tetramethylcyclobutane-1,3-dione, is hydrogenated to thecorresponding 2,2,4,4-tetraalkylcyclobutane-1,3-diol, for example,2,2,4,4-tetramethylcyclobutane-1,3-diol.

The alkyl radicals R₁, R₂, R₃, and R₄ on the2,2,4,4-tetraalkylcyclobutane-1,3-dione may each independently have 1 to8 carbon atoms. 2,2,4,4-tetraalkylcyclobutane-1,3-diones that aresuitably reduced to the corresponding diols include, but are not limitedto, 2,2,4,4,-tetramethylcyclobutane-1,3-dione,2,2,4,4-tetraethylcyclobutane-1,3-dione,2,2,4,4-tetra-n-propylcyclobutane-1,3-dione,2,2,4,4-tetra-n-butylcyclobutane-1,3-dione,2,2,4,4-tetra-n-pentylcyclobutane-1,3-dione,2,2,4,4-tetra-n-hexylcyclobutane-1,3-dione,2,2,4,4-tetra-n-heptylcyclobutane-1,3-dione,2,2,4,4-tetra-n-octylcyclobutane-1,3-dione,2,2-dimethyl-4,4-diethylcyclobutane-1,3-dione,2-ethyl-2,4,4-trimethylcyclobutane-1,3-dione,2,4-dimethyl-2,4-diethyl-cyclobutane-1,3-dione,2,4-dimethyl-2,4-di-n-propylcyclobutane-1,3-dione,2,4-n-dibutyl-2,4-diethylcyclobutane-1,3-dione,2,4-dimethyl-2,4-diisobutylcyclobutane-1,3-dione, and2,4-diethyl-2,4-diisoamylcyclobutane-1,3-dione.

The corresponding 2,2,4,4-tetraalkylcyclobutane-1,3-diols that may beused as the TACD compound include2,2,4,4-tetramethylcyclobutane-1,3-diol (“TMCD”),2,2,4,4-tetraethylcyclobutane-1,3-diol,2,2,4,4-tetra-n-propylcyclobutane-1,3-diol,2,2,4,4-tetra-n-butylcyclobutane-1,3-diol,2,2,4,4-tetra-n-pentylcyclobutane-1,3-diol,2,2,4,4-tetra-n-hexylcyclobutane-1,3-diol,2,2,4,4-tetra-n-heptylcyclobutane-1,3-diol,2,2,4,4-tetra-n-octylcyclobutane-1,3-diol,2,2-dimethyl-4,4-diethylcyclobutane-1,3-diol,2-ethyl-2,4,4-trimethylcyclobutane-1,3-diol,2,4-dimethyl-2,4-diethyl-cyclobutane-1,3-diol,2,4-dimethyl-2,4-di-n-propylcyclobutane-1,3-diol,2,4-n-dibutyl-2,4-diethylcyclobutane-1,3-diol,2,4-dimethyl-2,4-diisobutylcyclobutane-1,3-diol, and2,4-diethyl-2,4-diisoamylcyclobutane-1,3-diol. Desirably the TACDcompound comprises 2,2,4,4-tetramethylcyclobutane-1,3-diol.

The alkyl radicals R₁, R₂, R₃, and R₄ on the2,2,4,4-tetraalkylcyclobutane-1,3-diol may each independently have 1 to6 carbon atoms, or 1 to 5 carbon atoms, or 1 to 4 carbon atoms, or 1 to3 carbon atoms, or 1 to 2 carbon atoms. Or, the alkyl radicals R₁, R₂,R₃, and R₄ on the 2,2,4,4-tetraalkylcyclobutane-1,3-diol may each have 1carbon atom.

The hydrogenation of 2,2,4,4-tetraalkylcyclobutane-1,3-dione typicallyproduces cis-2,2,4,4-tetraalkylcyclobutane-1,3-diol andtrans-2,2,4,4-tetraalkylcyclobutane-1,3-diol. The cis/trans molar ratioof any of the species of TACD may range from 1.7 to 0.0 or 1.6 to 0.0 or1.5 to 0.0 or 1.4 to 0.0 or 1.3 to 0.0 or 1.2 to 0.0 or 1.1 to 0.0 or1.0 to 0.0 or 0.9 to 0.0 or 0.8 to 0.0 or 0.7 to 0.0 or 0.6 to 0.0 or0.5 to 0.0 or 0.4 to 0.0 or 0.3 to 0.0 or 0.2 to 0.0 or 0.1 to 0.0. Thecis/trans molar ratio may range from 1.7 to 0.1 or 1.6 to 0.1 or 1.5 to0.1 or 1.4 to 0.1 or 1.3 to 0.1 or 1.2 to 0.1 or 1.1 to 0.1 or 1.0 to0.1 or 0.9 to 0.1 or 0.8 to 0.1 or 0.7 to 0.1 or 0.6 to 0.1 or 0.5 to0.1 or 0.4 to 0.1 or 0.3 to 0.1 or 0.2 to 0.1. Or cis/trans molar ratiomay range from 1.7 to 0.2 or 1.6 to 0.2 or 1.5 to 0.2 or 1.4 to 0.2 or1.3 to 0.2 or 1.2 to 0.2 or 1.1 to 0.2 or 1.0 to 0.2 or 0.9 to 0.2 or0.8 to 0.2 or 0.7 to 0.2 or 0.6 to 0.2 or 0.5 to 0.2 or 0.4 to 0.2 or0.3 to 0.2.

The moles of TACD residues added to the melt phase process, based on 100mole % of the hydroxyl component, may be at least 20 mole %, or at least30 mole %, or at least 40 mole %, or at least 50 mole %, or at least 60mole %, or at least 70 mole %, or at least 80 mole %, and less than 90mole %, or less than 85 mole %, or less than 80 mole %, or less than 75mole %, or less than 70 mole %, or less than 65 mole %, based on allmoles of the hydroxyl component added. Suitable ranges include 20-90, or20-85, or 20-80, or 20-75, or 20-70, or 20-65, or 30-90, or 30-85, or30-80, or 30-75, or 30-70, or 30-65, or 30-60, or 40-90, or 40-85, or40-80, or 40-75, or 40-70, or 40-65, or 40-60, or 50-90, or 50-85, or50-80, or 50-75, or 50-70, or 50-65, or 50-60, or 60-90, or 60-85, or60-80, or 60-75, or 60-70, or 60-65, or 70-90, or 70-85, or 70-80, or70-75, or 80-90, or 80-85, in each case as a mole % based on the molesof the hydroxyl component.

The mole % of residues of TACD present in the copolyester, based on themoles of all residues in the copolyester, may be at least 10 mole %, orat least 15 mole %, or at least 20 mole %, or at least 25 mole %, or atleast 30 mole %, or at least 35 mole %, or at least 40 mole %, and lessthan 45 mole %, or less than 40 mole %, or less than 35 mole %, or lessthan 30 mole %. Suitable ranges include 10-45, or 15-45, or 20-45, or25-45, or 30-45, or 35-45, or 40-45, or 10-40, or 15-40, or 20-40, or25-40, or 30-40, or 35-40, or 10-35, or 15-35, or 20-35, or 25-35, or30-35, or 10-30, or 15-30, or 20-30, or 25-30, or 10-25, or 15-25, or20-25, or 15-20, in each case based on the moles of all residues in thecopolyester.

The copolyester also contains residues of neopentyl glycol, or2,2-dimethyl-1,3-propanediol (“NPG”). The amount of NPG added to themelt phase process, based on the amount of 100 mole % of the hydroxylcomponent, is at least 10 mole %, or at least 15 mole %, or at least 20mole %, or at least 30 mole %, or at least 40 mole %, or at least 50mole %, or at least 60 mole %, or at least 70 mole %, and less than 80mole %, or less than 75 mole %, or less than 70 mole %, or less than 65mole %, or less than 60 mole %, or less than 55 mole %, or less than 50mole %, or less than 45 mole %. Suitable ranges include 10-80, or 10-75,or 10-70, or 10-65, or 10-60, or 10-60, or 10-55, or 10-50, or 10-45, or20-80, or 20-75, or 20-70, or 20-65, or 20-60, or 20-65, or 20-60, or20-55, or 20-50, or 20-45, or 30-80, or 30-75, or 30-70, or 30-65, or30-60, or 30-55, or 30-50, or 30-45, or 40-80, or 40-75, or 40-70, or40-65, or 40-60, 40-55, or 40-50, or 40-45, or 50-80, or 50-75, or50-70, or 50-65, or 50-60, or 60-80, or 60-75, or 60-70, or 60-65, or70-80, or 70-75, or 80-90, or 80-85, in each case as a mole % based onthe moles of the hydroxyl component.

The mole % of residues of NPG present in the copolyester, based on themoles of all residues in the copolyester, may be at least 5 mole %, orat least 7 mole %, or at least 8 mole %, or at least 10 mole %, or atleast 15 mole %, or at least 20 mole %, or at least 25 mole %, or atleast 30 mole %, or at least 35 mole %, or at least 40 mole %, and lessthan less than 40 mole %, or less than 35 mole %, or less than 30 mole%. Suitable ranges include 5 to 40, or 7 to 40, or 8 to 40, or 10-40, or15-40, or 20-40, or 25-40, or 30-40, or 35-40, 5 to 35, or 7 to 35, or 8to 35, or 10-35, or 15-35, or 20-35, or 25-35, or 30-35, or 5 to 30, or7 to 30, or 8 to 30, or 10-30, or 15-30, or 20-30, or 25-30, or 5 to 25,or 7 to 25, or 8 to 25, or 10-25, or 15-25, or 20-25, or 5 to 20, or 7to 20, or 8 to 20, or 15-20, in each case as a mole % based on the molesof the copolyester polymer.

The copolyester composition also contains aluminum atoms. Desirably, thealuminum atoms are present as residues of an aluminum catalyst added tothe melt phase process for making the copolyester polymer, and theoxidation state, morphological state, structural state, or chemicalstate of the aluminum compound as added or of the residue present in thecomposition is not limited. The aluminum residue may be in a formidentical to the aluminum compound as added to the melt phase reaction,but may be altered since the aluminum participates in accelerating therate of polycondensation. By the term “aluminum atoms” or “aluminum” ismeant the presence of aluminum in the copolyester polymer detectedthrough any suitable analytical technique regardless of the oxidationstate of the aluminum. Suitable detection methods for the presence ofaluminum include inductively coupled plasma optical emissionspectroscopy (ICP-OES). The concentration of aluminum is reported as theparts per million of metal atoms based on the weight of the polymer. Theterm “metal” does not imply a particular oxidation state.

Aluminum may be added to the melt phase process (the method of additionnot being limited and including adding the aluminum compound to thecatalyst mix tank of the melt phase process, feeding to directly a meltphase vessel, or feeding into pipes connecting vessels) as a compound(which includes a salt or a complex), or as a metal provided that it isultimately active as a catalyst in the polycondensation phase eitheralone or in combination with the alkali metal or alkaline earth metalatoms or compounds. It is desirable to select an aluminum compound whichcan be dissolved in a diluent or a carrier that is volatile and/orreactive with the copolyester forming ingredients. Suitable liquidreactive carriers can have any molecular weight, such as those rangingfrom 62 to about 10,000 grams per mole. Aluminum compounds can also beadded as slurries or suspensions in a liquid that is volatile and/orreactive with the copolyester forming ingredients. Aluminum can also beadded to the melt phase process by melt blending the aluminum compoundwith a copolyester polymer in a suitable extruder or other device toform a concentrate, and subsequently, preferably melting the concentrateas a molten feed to the melt phase process. A preferred mode of additionof aluminum compounds is addition to a catalyst mix tank, which is partof the copolyester melt phase process equipment. Preferably, thecatalyst mix tank also contains an alkali metal compound or an alkalineearth compound or alkali compound as well as a suitable solvent. Asuitable solvent can include any of the hydroxyl compounds used asreactants to make the copolyester. A desirable solvent is ethyleneglycol. Alternatively, a solvent consisting of a 50/50 w/w/mixture ofethylene glycol and neopentyl glycol is also desirable.

For example, an aluminum compound and an alkali metal compound or analkaline earth metal compound or an alkali compound can be heated at atemperature and for an amount of time to affect dissolution initially.Suitable temperatures include 110 to 140° C., or 115 to 135° C., for oneto four hours. A nitrogen purge can minimize color formation in thesolution or mixture if color bodies are a problem. The nitrogen purgerate should be sufficient to remove volatiles that react to form colorbodies, such as from 0.5 to 3 scfm, or 1 to 2 scfm. To maintain orimprove solubility, it is helpful to keep the solution or mixture at 115to 135° C. with a nitrogen purge. The contents of the catalyst mix tankmay be transferred to a catalyst feed tank, which may be utilized tointroduce the solution or mixture into the copolyester melt phasemanufacturing process. The catalyst mix can be filtered to remove anyinsoluble material prior to feeding to the polymerization process.

Aluminum compounds of the invention are catalytically active.

Examples of aluminum compounds include aluminum compounds with at leastone organic substituent. Illustrative examples of suitable compoundsinclude those of the formula:Al[OR]_(a)[OR′]_(b)[OR″]_(c)[R′″]_(d)wherein R, R′, R″ are independently an alkyl group, aryl group, acylgroup or hydrogen, where preferably at least one of R, R′ R″ and R′″ isnot hydrogen, R′″ is an anionic group, and a, b, c, d are independently0 or positive integers, and a+b+c+d is equal to 3 or no greater than 3.

Suitable examples of aluminum compounds include the carboxylic acidsalts of aluminum such as aluminum acetate (if solubilized), aluminumbenzoate, aluminum lactate, aluminum laurate, aluminum stearate,aluminum alcoholates such as aluminum ethylate, aluminum isopropylate(also known as aluminum isopropoxide), aluminum tri n-butyrate, aluminumtri-tert-butyrate, mono-sec-butoxyaluminum diisopropylate, and aluminumchelates in which the alkoxy group of an aluminum alcoholate ispartially or wholly substituted by a chelating agents such as an alkylacetoacetate or acetylacetone such as ethyl acetoacetate aluminumdiisopropylate, aluminum tris(ethyl acetoacetate), alkyl acetoacetatealuminum diisopropylate, aluminum monoacetylacetate bis(ethylacetoacetate), aluminum tris(acetyl acetate), aluminum acetylacetonate.

Desirable among the aluminum compounds is aluminum isopropoxide

The amount of aluminum atoms present in the copolyester polymergenerally ranges from at least 5 ppm, or at least 8 ppm, or at least 10ppm, or at least 15 ppm, or at least 20 ppm, or at least 25 ppm, or atleast 30 ppm, or at least 35 ppm, or at least 40 ppm, or at least 45ppm, or at least 50 ppm, and less than 100 ppm, or less than 90 ppm, orless than 80 ppm, or less than 75 ppm, or less than 70 ppm, or less than65 ppm, or less than 60 ppm, or less than 55 ppm Al based on the weightof the polymer.

Desirably, the range of aluminum atoms by weight is from 10 ppm to 100ppm, or 20 ppm to 100 ppm, or 25 ppm to 100 ppm, or 30 ppm to 100 ppm,or 35 ppm to 100 ppm, or 40 ppm to 100 ppm, or 45 ppm to 100 ppm, or 50ppm to 100 ppm, or 10 ppm to 75 ppm, or 15 ppm to 75 ppm, or 20 ppm to75 ppm, or 25 ppm to 75 ppm, or 30 ppm to 75 ppm, or 35 ppm to 75 ppm,or 40 ppm to 75 ppm, or 45 ppm to 75 ppm, or 50 ppm to 75 ppm, or 10 ppmto 65 ppm, or 20 ppm to 65 ppm, or 30 ppm to 65 ppm, or 35 ppm to 65ppm, or 40 ppm to 65 ppm, or 45 ppm to 65 ppm, 10 ppm to 50 ppm, or 20ppm to 50 ppm, or 30 ppm to 50 ppm, or 35 ppm to 50 ppm, or 40 ppm to 50ppm, 10 ppm to 40 ppm, or 20 ppm to 40 ppm, or 30 ppm to 40 ppm, or 10ppm to 35 ppm, or 20 ppm to 35 ppm, or 30 ppm to 35 ppm, or 10 ppm to 30ppm, or 20 ppm to 30 ppm based on the weight of the copolyester.

The copolyester composition contains an alkali metal residue or analkaline earth metal residue, in any form or oxidation state. Theiroxidation states or ultimate physical, morphological, structural, orchemical states are not limited. The word “alkali metal” or “alkalineearth metal” or “metal” includes the atom in its elemental state or inan oxidation state corresponding to its allowable valences in itsPeriodic group. The chemical state of the alkali upon addition is alsonot limited. The alkali may be added as a metal compound, organometalliccompound, or as a compound without a metal. Likewise, the chemical stateof the alkaline earth metal compound or alkali metal compound uponaddition is not limited.

The alkali metals and alkaline earth metals include the metals in GroupIA and Group IIA or the periodic table, including but not limited to Li,Na, K, Rb, Cs, Mg, Ca, Sr, and preferably Li, Na or K. The metals may beadded to the melt phase as metal compounds (which includes a complex ora salt) having counterions, among which the preferred ones arehydroxides, carbonates, and carboxylic acids.

Desirably, the amount of Group 1A or IIA metal atoms is within a rangeof from 5 ppm to 75 ppm, or 10 ppm to 60 ppm, or 15 ppm to 50 ppm, or 20ppm to 50 ppm, or 25 ppm to 50 ppm, or 5 ppm to 45 ppm, or 10 ppm to 45ppm, or 15 ppm to 45 ppm, or 20 ppm to 45 ppm, or 25 ppm to 45 ppm, or 5ppm to 40 ppm, or 10 ppm to 40 ppm, or 15 ppm to 40 ppm, or 20 ppm to 40ppm, or 25 ppm to 40 ppm, or 5 ppm to 35 ppm, or 10 ppm to 35 ppm, or 15ppm to 35 ppm, or 20 ppm to 35 ppm, or 25 ppm to 35 ppm, or 5 ppm to 30ppm, or 10 ppm to 30 ppm, or 15 ppm to 30 ppm, or 20 ppm to 30 ppm. Ineach case, the metal is desirably an alkali metal such as Li.

The ratio of the moles of alkali metal or moles of alkaline earth metalto the moles of aluminum (M:Al) is not limited but desirably ranges fromat least 0.1, or at least 0.25, or at least 0.5, or at least 0.75, or atleast 1, or at least 2, and less than about 15, less than about 10, lessthan about 7, less than about 6, less than about 5. Desirably, the M:Almolar ratio is at least 1.5, or at least 2 and less than 7.

The copolyester also contains tin atoms. The tin atoms from the tincatalyst are useful to improve the insertion of TMCD into the polymerbackbone. By improving the insertion of TMCD into the backbone, theprocess is economically advantageous by avoiding the use of largeexcesses of TMCD charges to the esterification zone that are required toobtain the desired target amount of TMCD into the copolyester, or byusing the same charge, results in an increased level of TMCD insertedinto the copolyester, thereby improving the Tg of the copolyester.

Tin atoms may be added to the melt phase process (the method of additionnot being limited and including adding the tin compound to the catalystmix tank of the melt phase process, feeding to directly a melt phasevessel, or feeding into pipes connecting vessels, feeding to the firstesterification vessel, and feeding as the first catalyst to the meltphase process prior to addition of aluminum and alkali or alkaline earthmetal catalysts) as a compound (which includes a salt or a complex), oras a metal provided that they are ultimately active as a catalyst in thepolycondensation phase either alone or in combination with the aluminum,alkali metal and/or or alkaline earth metal atoms or compounds. At leasta portion of the tin atoms of the invention are catalytically active ascompounds or metals. It is desirable to select a tin catalyst compoundwhich can be dissolved in a diluent or a carrier that is volatile and/orreactive with the copolyester forming ingredients, or that is a liquidat ambient temperatures and can be fed directly to the process as aliquid; or as a low-melting solid that can be heated to form a liquidwith can be fed directly to the process. Suitable liquid reactivecarriers can have any molecular weight, such as those ranging from 62 toabout 10,000 grams per mole. Tin compounds can also be added as slurriesor suspensions in a liquid that is volatile and/or reactive with thecopolyester forming ingredients. Tin can also be added to the melt phaseprocess by melt blending the tin compound with a copolyester polymer ina suitable extruder or other device to form a concentrate, andsubsequently, preferably melting the concentrate as a molten feed to themelt phase process. A preferred mode of addition of tin compounds isaddition to a catalyst mix tank, which is part of the copolyester meltphase process equipment. A suitable solvent can include any of thehydroxyl compounds used as reactants to make the copolyester.

For example, a tin compound, an aluminum compound and an alkali metalcompound or an alkaline earth metal compound can be heated at atemperature and for an amount of time to affect dissolution initially.Suitable temperatures include 110 to 140° C., or 115 to 135° C., for oneto four hours. A nitrogen purge can minimize color formation in thesolution or mixture if color bodies are a problem. The nitrogen purgerate should be sufficient to remove volatiles that react to form colorbodies, such as from 0.5 to 3 scfm, or 1 to 2 scfm. To maintain orimprove solubility, it is helpful to keep the solution or mixture at 115to 135° C. with a nitrogen purge. The contents of the catalyst mix tankmay be transferred to a catalyst feed tank, which may be utilized tointroduce the solution or mixture into the copolyester melt phasemanufacturing process.

Desirably, the tin catalyst is added to the melt phase manufacturingprocess, and specifically during esterification before the addition ofthe aluminum atoms and the alkali or alkaline earth metal atoms. Forexample, the tin atoms that form part of the tin catalyst can be mixedwith one or more of the acid component and/or hydroxyl component whichare fed to the esterification process or the first esterificationvessel. After reacting the acid component and hydroxyl component to forma reaction mixture after at least 1 minute of reaction time, or at least5 minutes, or at least 15 minutes, or at least 20 minutes, the aluminumand alkali or alkaline earth metal catalyst can be added to the reactionmixture. This is particularly desirable when high catalyst loadings oftin are utilized. By adding tin catalysts first, one may achieve acopolyester that has a good IV and/or reduce the residence time of themelt in the finisher vessel or zone.

Suitable examples of tin compounds include the organotin salts, theorganotin oxides, and stannoic acids For example, see U.S. Pat. No.2,720,507, where the portion concerning tin catalysts is incorporatedherein by reference. These catalysts are tin compounds containing atleast one organic radical. These catalysts include compounds of bothdivalent or tetravalent tin which have the general formulas set forthbelow:

M₂(Sn(OR)₄) A. MH(Sn(OR)₄) B. M′(Sn(OR)₄) C. M′(HSn(OR)₄)₂ D.M₂(Sn(OR)₆) E. MH(Sn(OR)₆) F. M′(Sn(OR)₆) G. M′(HSn(OR)₆)₂ H. Sn(OR)₂ I.Sn(OR)₄ J. SnR′₂ K. SnR′₄ L. R′₂SnO M.

wherein M is an alkali metal, e.g. lithium, sodium, or potassium, M′ isan alkaline earth metal such as Mg, Ca or Sr, each R represents an alkylradical containing from 1 to 8 carbon atoms, each R′ radical representsa substituent selected fromthose consisting of alkyl radicals containing from 1 to 8 carbon atoms(i.e. R radicals) and aryl radicals of the benzene series containingfrom 6 to 9 carbon atoms (e.g. phenyl, tolyl, benzyl, phenyl ethyl,etc., radicals), and Ac represents an acyl radical derived from anorganic acid containing from 2 to 18carbon atoms (e.g. acetyl, butyryl, lauroyl, benzoyl, stearoyl, etc.).

Bimetallic alkoxide catalysts can be made as described by Meerwein, Ann.476, 113 (1929). As shown by Meerwein, these catalysts are not merelymixtures of the two metallic alkoxides. They are definite compoundshaving a salt-like structure. These are the compounds depicted above bythe Formulas A through H. Those not specifically described by Meerweincan be prepared by procedures analogous to the working examples andmethods set forth by Meerwein. The other tin compounds can also be madeby various methods such as those described in the following literature:

For the preparation of diaryl tin dihalides (Formula P) see Ber. 62, 996(1929); J. Am. Chem. Soc. 49, 1369 (1927). For the preparation ofdialkyl tin dihalides (Formula P) see J. Am. Chem. Soc. 47, 2568 (1925);c.A. 41, 90 (1947). For the preparation of diaryl tin oxides (Formula M)see J. Am. Chem. Soc. 48, 1054 (1926). For the preparation of tetraaryltin compounds (Formula K) see c.A. 32, 5387 (1938). For the preparationof tin alkoxides (Formula J) see c.A. 24, 586.1930).

For the preparation of alkyl tin salts (Formula Q) see c.A. 31, 4290.For the preparation of alkyl tin compounds see c.A. 35, 2470 (1941):c.A. 33, 5357 (1939). For the preparation of mixed alkyl aryl tin(Formulas K and L) see c.A. 31, 4290 (1937): c.A. 38, 331 (1944). Forthe preparation of other tin compounds not covered by these citationssee “Die Chemie der Metal-Organischen Verbindungen.” by Krause and V.Grosse, published in Berlin, 1937, by Gebroder-Borntrager.

The tin alkoxides (Formulas I and J) and the bimetallic alkoxides(Formulas A through H) contain R substituents which can represent bothstraight chain and branched chain alkyl radicals, e.g. diethoxide,tetramethoxide, tetrabutoxide, tetra-tert-butoxide, tetrahexoxide, etc.

The alkyl derivatives (Formulas K and L) contain one or more alkylradicals attached to a tin atom through a direct C—Sn linkage, e.g.dibutyl tin, dihexyl tin, tetra-butyl tin, tetraethyl tin, tetramethyltin, dioctyl tin, etc. Two of the tetraalkyl radicals can be replacedwith an oxygen atom to form compounds having Formula M, e.g. dimethyltin oxide, diethyl tin oxide, dibutyl tin oxide, diheptyl tin oxide,etc. In one embodiment, the tin catalyst comprises dimethyl tin

oxide.

Complexes can be formed by reacting dialkyl tin oxides with alkali metalalkoxides in an alcohol solution to form compounds having Formula N,which compounds are especially useful catalysts, e.g. react dibutyl tinoxide with sodium ethoxide, etc. This formula is intended to representthe reaction products described. Tin compounds containing alkyl andalkoxy radicals are also useful catalysts (see Formula 0), e.g. diethyltin diethoxide, dibutyl tin dibutoxide, dihexyl tin dimethoxide, etc.

Salts derived from dialkyl tin oxides reacted with carboxylic acids orhydrochloric acid are also of particular value as catalysts; seeFormulas P and Q. Examples of these catalytic condensing agents includedibutyl tin diacetate, diethyl tin dibutyrate, dibutyl tin dilauroate,dimethyl tin dibenzoate, dibutyl tin dichloride, diethyl tin dichloride,dioctyl tin dichloride, dihexyl tin distearate, etc.

The tin compounds having Formulas K, Land M can be prepared wherein oneor more of the R′ radicals represents an aryl radical of the benzeneseries, e.g. phenyl, tolyl, benzyl, etc. Examples include diphenyl tin,tetraphenyl tin, diphenyl dibutyl tin, ditolyl diethyl tin, diphenyl tinoxide, dibenzyl tin,

tetrabenzyl tin, di([B-phenylethyl)-tin oxide, dibenzyl tin oxide, etc,

The amount of tin atoms present in the copolyester polymer generallyranges from at least 3 ppm, or at least 5 ppm, or at least 8 ppm, or atleast 10 ppm, or at least 15 ppm, or at least 20 ppm, or at least 30ppm, and less than 100 ppm, or less than 100 ppm, or up to 75 ppm, or upto 65 ppm or up to 60 ppm or up to 50 ppm or up to 45 ppm tin based onthe weight of the polymer.

Suitable exemplary ranges include from 3 ppm to 100 ppm, or 3 ppm to 75ppm, or 3 ppm to 65 ppm, or 3 ppm to 60 ppm, or 3 ppm to 50 ppm, or 3ppm to 45 ppm, or 5 ppm to 100 ppm, or 5 ppm to 75 ppm, or 5 ppm to 65ppm, or 5 ppm to 60 ppm, or 5 ppm to 50 ppm, or 5 ppm to 45 ppm, or 10ppm to 75 ppm, or 10 ppm to 65 ppm, or 10 ppm to 60 ppm, or 10 ppm to 50ppm, or 10 ppm to 45 ppm, or 20 ppm to 75 ppm, or 20 ppm to 65 ppm, or20 ppm to 60 ppm, or 20 ppm to 50 ppm, or 20 ppm to 45 ppm, or 30 ppm to75 ppm, or 30 ppm to 65 ppm, or 30 ppm to 60 ppm, or 30 ppm to 50 ppm,or 30 ppm to 45 ppm.

The order of addition of catalyst metals is not limited. The aluminum,alkali or alkaline earth metal atoms, and tin atoms may be addedtogether or as separate streams, together with acid component or thehydroxyl component prior to feeding one or both to the firstesterification vessel, or fed together or separately into a firstesterification vessel separate from the feed of the acid component orthe hydroxyl component, or fed sequentially. For example, the tin atomsmay be pre-mixed together with the acid component, which can be formedinto a paste, and the paste fed into the first esterification vessel,followed by feeding the aluminum and alkali or alkaline earth metalatoms into the last esterification vessel, into a line or vessel betweenthe esterification phase and the polycondensation phase, or at or intothe polycondensation phase vessels or lines.

To avoid potential undesirably side reactions between aluminum catalystand water generated in the esterification zone which may inhibit ordeactivate the aluminum catalyst and thereby slow down the rate ofpolycondensation, it is desirable in yet another embodiment to add thealuminum compounds after substantial completion of the esterificationreaction or at the beginning of or during polycondensation. In a furtherembodiment, at least 75%, or at least 85%, or at least 95% of theesterification reaction (in terms of conversion) is conducted in theabsence of added aluminum compounds. It is desirable to add the aluminumcompound and the alkali metal or alkaline earth metal compound at ornear the same addition point. It is most desirable to premix and heatthe aluminum compound and the alkali metal or alkaline earth metalcompound, like in a catalyst mix tank, prior to addition to the meltphase manufacturing line for copolyester polymers.

Other catalyst metals may be present if desired. For example, Mn, Zn,Sb, Co, Ti, and Ge catalysts may be used in conjunction with aluminumand alkaline earth metals or alkali catalysts. Titanium and zinccatalysts can be used, particularly if melt phase manufacture involvesester exchange reactions. The amount of titanium catalyst, if used,generally ranges from 2 ppm to 30 ppm, based on the weight of thepolymer. Zinc catalysts can also be used in combination with theSn/Al/alkali or alkaline earth metal system of the invention in amountsthat are the same as the amounts from 30 to 80 ppm. It may be necessaryto add a stabilizer such as a phosphorus compound If catalytic metalsother than aluminum, alkaline earth metals, or alkali metals arepresent.

Desirably, the copolyester polymer is made without the addition oftitanium catalyst, cobalt catalyst, zinc catalyst or antimony catalystto the melt phase reaction. More preferably, the copolyester polymer ismade without the addition of any catalytically active metal or metalcompounds to the melt phase reaction other than the tin/aluminum/alkalimetal or alkaline earth or alkali system It is to be recognized,however, that one or more of metals such as cobalt or manganese willmost likely be present at low levels in the melt because they come asimpurities with the terephthalic acid composition made from ametal-catalyzed, liquid-phase oxidation process. Metal impuritiespresent in the raw material supply to the melt phase process are notconsidered to be metals added to the melt phase process.

The weight of aluminum and alkaline earth metal or alkali metal and tinand other co-catalyst metals can be measured upon addition to the meltphase or by analytical techniques for detecting the amount in thefinished polymer or article. Suitable detection methods for the presenceof aluminum and alkali metals or alkaline earth metals includeinductively coupled plasma optical emission spectroscopy (ICP-OES).While X-ray fluorescence spectroscopy (XRF) is a suitable detectionmethod for some alkaline earth metals and some alkali metals, it is notsuitable for detecting aluminum at lower levels, like those found incopolyester. The concentration of an alkaline earth metal or an alkalimetal is reported as the parts per million of metal atoms based on theweight of the polymer.

The aluminum and alkali or alkaline earth metals may be added as asolution, fine dispersion, a paste, a slurry, or neat. They arepreferably added as a liquid, a melt, or a free flowing solid which canbe metered. Most preferably they are added as a liquid, and inparticular as a liquid solution or dispersion.

Optionally, the copolyester polymer also contains a stabilizer. By acatalyst stabilizer is meant a compound effective to at least partiallydeactivate or inhibit the activity of the catalyst system. Stabilizersuseful in the invention can be phosphorus-based acids wherein one ormore of the hydrogen atoms of the acid compound (bonded to either oxygenor phosphorus atoms) are replaced with alkyl, branched alkyl,substituted alkyl, alkyl ethers, substituted alkyl ethers, alkyl-aryl,alkyl-substituted aryl, aryl, substituted aryl, and mixtures thereof.The esters can contain alkyl, branched alkyl, substituted alkyl, alkylethers, aryl, and/or substituted aryl groups. The esters can also haveat least one alkyl group and at least one aryl group. The number ofester groups present in the particular phosphorus compound can vary fromzero up to the maximum allowable based on the number of hydroxyl groupspresent on the phosphorus compound used. For example, an alkyl phosphateester can include one or more of the mono-, di-, and tri alkyl phosphateesters; an aryl phosphate ester includes one or more of the mono-, di-,and tri aryl phosphate esters; and an alkyl phosphate ester and/or anaryl phosphate ester also include, but are not limited to, mixed alkylaryl phosphate esters having at least one alkyl and one aryl group.

The stabilizers useful in the invention include alkyl, aryl or mixedalkyl aryl esters or partial esters of phosphoric acid, phosphorus acid,phosphinic acid, phosphonic acid, or phosphonous acid. The alkyl or arylgroups can contain one or more substituents.

For example, the phosphorus compounds can be at least one of substitutedor unsubstituted alkyl phosphate esters, substituted or unsubstitutedaryl phosphate esters, substituted or unsubstituted mixed alkyl arylphosphate esters, diphosphites, salts of phosphoric acid, phosphineoxides, and mixed aryl alkyl phosphites, reaction products thereof, andmixtures thereof. The phosphate esters include esters in which thephosphoric acid is fully esterified or only partially esterified.

The phosphate esters include esters in which the phosphoric acid isfully esterified or only partially esterified. In one embodiment, forexample, the thermal stabilizers useful in the invention can include atleast one phosphate ester.

The phosphate esters can include alkyl, alkoxy-alkyl, phenyl, orsubstituted phenyl groups. These phosphate esters are generally referredto herein as alkyl and/or aryl phosphate esters. Certain preferredembodiments include trialkyl phosphates, triaryl phosphates, alkyldiaryl phosphates, dialkyl aryl phosphates, and mixtures of suchphosphates, wherein the alkyl groups are preferably those containingfrom 2 to 12 carbon atoms, and the aryl groups are preferably phenyl.

Representative alkyl and branched alkyl groups are those containing from1-12 carbon atoms, including but not limited to, ethyl, propyl,isopropyl, butyl, hexyl, cyclohexyl, 2-ethylhexyl, octyl, decyl anddodecyl. Substituted alkyl groups include, but are not limited to, thosecontaining at least one of carboxylic acid groups and esters thereof,hydroxyl groups, amino groups, keto groups, and the like.

Representative of alkyl-aryl and substituted alkyl-aryl groups are thosewherein the alkyl portion contains from 1-12 carbon atoms, and the arylgroup is phenyl or substituted phenyl wherein groups such as alkyl,branched alkyl, aryl,

hydroxyl, and the like are substituted for hydrogen at any carbonposition on the phenyl ring. Aryl groups include phenyl or substitutedphenyl wherein groups such as alkyl, branched alkyl, aryl, hydroxyl andthe like are substituted

for hydrogen at any position on the phenyl ring.

Other useful phosphate esters include dibutylphenyl phosphate, triphenylphosphate, tricresyl phosphate, tributyl phosphate, tri-2-ethylhexylphosphate, trioctylphosphate, and/or mixtures thereof, includingparticularly mixtures of tributyl phosphate and tricresyl phosphate, andmixtures of isocetyl diphenyl phosphate and 2-ethylhexyl diphenylphosphate.

Examples of aryl phosphates include Merpol A. Merpol A is a phosphateester commercially available from Stepan Chemical Co and/or E.I. duPontde Nemours & Co. The CAS Registry number for Merpol A is believed to be30 CAS Registry #37208-27-8.

Amounts of stabilizer added during polymerization or post manufacturing,if added, can include but are not limited to: 1 to 200 ppm, 1 to 150ppm, 1 to 100 ppm; 1 to 50 ppm, 1 to 30 ppm, 1 to 20 ppm, 1 to 15 ppm, 1to 10 ppm, 1 to 8 ppm, 1 to 5 ppm, or 1 to 3 ppm, based on the totalweight of the polyester composition.

The copolyesters can be made by continuous, semi-continuous, and batchmodes of operation and may utilize a variety of reactor types. Examplesof suitable reactor types include, but are not limited to, stirred tank,continuous stirred tank, slurry, tubular, wiped-film, falling film, orextrusion reactors. The term “continuous” as used herein means a processwherein reactants are introduced and products withdrawn simultaneouslyin an uninterrupted manner. By “continuous” it is meant that the processis substantially or completely continuous in operation in contrast to a“batch” process. “Continuous” is not meant in any way to prohibit normalinterruptions in the continuity of the process due to, for example,start-up, reactor maintenance, or scheduled shut down periods. The term“batch” process as used herein means a process wherein all the reactantsare added to the reactor and then processed according to a predeterminedcourse of reaction during which no material is fed or removed into thereactor. The term “semicontinuous” means a process where some of thereactants are charged at the beginning of the process and the remainingreactants are fed continuously as the reaction progresses.Alternatively, a semicontinuous process may also include a processsimilar to a batch process in which all the reactants are added at thebeginning of the process except that one or more of the products areremoved continuously as the reaction progresses.

The copolyester compositions useful in the invention can be made byprocesses known from the literature such as, for example, by processesin homogenous solution, by trans-esterification processes in the melt,and by two phase interfacial processes. Suitable methods include, butare not limited to, the steps of reacting an acid component with thehydroxyl component at a temperature within a range of 100° C. to 315° C.and at a pressure within a range of 0.1 to 760 mm Hg. See U.S. Pat. No.3,772 and U.S. Pat. No. 2,720,507 for methods of producing polyesters,the disclosures of each which are hereby incorporated herein byreference.

For example, the process comprises the steps of:

-   -   (A) heating the acid component and the hydroxyl component in the        presence of at least one catalyst selected from a tin catalyst,        an aluminum catalyst, and a alkali or alkaline earth metal        catalyst, and optionally with a stabilizer to a temperature of        150 to 250° C. wherein:        -   (i) the acid component comprises at least 80 mole % of the            residues of terephthalic acid, or desirably residues of the            derivates of terephthalic acid; and        -   (ii) the hydroxyl component comprises at least 80 mole % of            the residues of NPG and TACD,        -   based on 100 mole percent of acid component residues and 100            mole percent of hydroxyl component residues in the            copolyester polymer; and    -   (B) polycondensing the product of Step (A) by heating it at a        temperature of 275 to 320° C. for 1 to 6 hours.

Reaction times for the esterification Step (A) are dependent upon theselected temperatures, pressures, and feed mole ratios of the hydroxylcomponent to the acid component. Step (A) can be carried out until 50%by weight or more of the TACD has been reacted. Step (A) may be carriedout under pressure, ranging from 0 psig to 100 psig.

In step (B), the reaction mixture can be placed under a pressureranging, from 0.002 psig to below atmospheric pressure, or by blowinghot nitrogen gas over the mixture.

As an example, one can make the copolyester by a process comprising;

-   -   (A) esterifying or trans-esterifying by heating a mixture to a        temperature ranging from 150° C. to 200° C. under a pressure        ranging from 0 psig to 75 psig wherein said mixture comprises:        -   (i) an acid component comprising at least 80 mole % of the            residues of terephthalic acid, or desirably residues of the            derivates of terephthalic acid; and        -   (ii) a hydroxyl component comprising at least 80 mole % of            the residues of NPG and TACD,        -   based on 100 mole percent of acid component residues and 100            mole percent of hydroxyl component residues in the            copolyester polymer.    -   wherein the molar ratio of hydroxyl component to the acid        component added in Step (A) is within a range of 1.0-1.5/1.0;        wherein the mixture in Step (A) is heated in the presence of at        least one catalyst comprising alkali or alkaline earth metal        atoms, aluminum atoms, and tin atoms; and    -   (B) polycondensing the product of Step (A) at a temperature of        275° C. to 320° C. for 1 to 6 hours, under a pressure within a        range of the final pressure of Step (A) down to 0.02 torr        absolute.

The stabilizer, reaction products thereof, and mixtures thereof can beadded either during esterification, polycondensation, or both and/or itcan be added post-polymerization. For example, the stabilizer can beadded during esterification, or both during esterification andpolycondensation, or only during polycondensation.

Reaction times for the esterification Step (A) are dependent upon theselected temperatures, pressures, and feed mole ratios of glycol todicarboxylic acid. The pressure used in Step (B) is at least onepressure chosen from 20 torr absolute to 0.02 torr absolute, or 10 torrabsolute to 0.02 torr absolute, or 5 torr absolute to 0.02 torrabsolute, or 3 torr absolute to 0.02 torr absolute; or 20 torr absoluteto 0.1 torr absolute; or 10 torr absolute to 0.1 torr absolute; or 5torr absolute to 0.1 torr absolute; or 3 torr absolute to 0.1 torrabsolute.

The molar ratio of hydroxyl bearing component to the acid component canbe adjusted to within 1.0-1.5/1.0; or 1.01-1.5/1.0; 1.01-1.3/1.0; or1.01-1.2/1.0; or 1.01-1.15/1.0; or 1.01-1.01-1.10/1.0; or 1.03-1.51, or1.0; or 1.03-1.3/1.0; or 1.03-1.2/1.0; or 1.03-1.151, or 1.0; or1.03-1.10/1.0; or 1.05-1.5/1.0; 1.05-1.31, or 1.05-1.2/1.0; or1.05-1.15/1.0; or 1.05-1.15/1.0; or 1.05-1.10/1.0.

The heating or residence time of the copolyester melt in Step (B), or inthe finisher vessel, may be from 1 to 6 hours, or 1 to 5 hours, or 1 to4 hours, or 1 to 3 hours, or 1.5 to 3 hours, or 1 to 2 hours.

The reaction temperature of the copolyester in Step B, or in thefinisher vessel (as determined by either the set point temperature orthe actual internals temperature) should be at least 275° C., and canalso be at least 278° C., or at least 279° C., or at least 280° C., orat least 283° C., or at least 285° C., or at least 287° C., or at least289° C., or at least 290° C., or at least 292° C., and up to 310° C., orup to 305° C., or up to 300° C., or up to 295° C., or up to 292° C., orup to 290° C., or up to 289° C., or up to 287° C.

In the process of the invention, the copolyester can be obtained byprocess comprising:

-   -   a) polycondensing a copolyester melt, comprising residues of NPG        and residues of TACD, to an IV of at least 0.55 dL/g in the        presence of alkali or alkaline earth metal atoms, aluminum        atoms, and tin atoms to obtain a high IV copolyester melt;    -   b) converting the high IV copolyester melt into amorphous        copolyester particles having a Tg of a least 90° C.

There is also provided a process for making a copolyester compositioncomprising polycondensing a copolyester melt, comprising residues of NPGand residues of TACD, to an IV of at least 0.55 dL/g in at a temperatureof at least 275° C. and converting copolyester melt into amorphouscopolyester particles having a Tg of a least 90° C. and which arethermally stable.

It is desirable to feed one or more dicarboxylic acids, preferablyaromatic dicarboxylic acids, or ester forming derivatives thereof, andone or more of the hydroxyl component continuously to an esterificationreactor operated at a temperature of between about 150° C. and 250° C.,and at a super-atmospheric pressure of between about 0 psig to 750 psig.The residence time of the reactants typically ranges from between aboutone and six hours. Normally, the esterification or trans-esterificationreaction is continued desirably until a an acid or ester groupconversion of at least 70% is achieved, but more typically until an acidor ester group conversion of at least 85% is achieved to make thedesired oligomeric mixture.

Water is removed as the esterification reaction proceeds in order todrive the equilibrium toward the desired products. Methanol is removedas the ester exchange reaction of a dimethyl ester of a dicarboxylicacid proceeds in order to drive the equilibrium toward the desiredproducts.

The esterification zone typically produces the oligomer species, if any,continuously in a series of one or more reactors. Alternately, theoligomer species in the oligomeric mixture could be produced in one ormore batch reactors. At this stage, the It.V. is usually not measurableor is less than 0.1 dL/g. The average degree of polymerization of themolten oligomeric mixture is typically less than 15, and often less than7.0.

Desirably, Step A or the esterification or transesterification reaction,or the whole melt phase process (includes esterification or esterexchange and polycondensation) reaction proceeds in the absence of addedtitanium compounds.

Once the oligomeric mixture is made to the desired percent conversion ofthe acid or ester groups, it is transported from the esterification zoneor reactors to the polycondensation zone (Step B). The commencement ofthe polycondensation reaction is generally marked by either a higheractual operating temperature than the operating temperature in theesterification zone, or a marked reduction in pressure (usuallysub-atmospheric) compared to the esterification zone, or both. Typicalpolycondensation reactions occur at temperatures ranging from about 230°C. and 320° C., and at sub-atmospheric pressure of between less than 760torr to about 0.2 torr. The residence time of the reactants duringpolycondensation typically ranges from between about 2 to about 6 hours.

In some processes, polycondensation reactions are initiated andcontinued in the melt phase in a prepolymerization zone and finished inthe melt phase in a finishing zone, after which the melt is solidifiedto form the copolyester polymer melt phase product, generally in theform of chips, pellets, or any other shape.

The temperature applied to the polymer melt or of the polymer melt in atleast a portion of the polycondensation zone is desirably greater than260° and less than about 290° C. The pressure in the final reactor (orfinishing zone) may be within the range of about 0.2 to 20 mm torr, or0.2 to 10 torr, or 0.2 to 2 torr.

It is desired that the aluminum compound and the alkali or alkalineearth metal compound are added close together e.g. both before the It.V.of the melt reaches 0.2 dL/g, or 0.1 dL/g, or before an increase of 0.1dL/g after exiting the last esterification reactor, or before enteringthe first polycondensation reaction vessel). The aluminum, alakali oralkaline earth metal and tin atoms can be added during Step (A), oradded together prior to the polycondensation zone, or added togetherbefore the I.V. of the melt phase product is 0.2 dL/g, or added beforeesterification or trans-esterification is 85% complete (by time) orbefore 75% completion or before 50% completion or before 30% completioneach by time. Preferably, the tin catalyst is added at the start ofester exchange to maximize TMCD incorporation followed by a lateraddition of the Li/Al catalysts added together

The aluminum compound and the alakali or alkaline earth metal compoundcan be heated together prior to introduction into a melt-phasecopolyester manufacturing line. Since aluminum operates as part of thepolycondensation catalyst system, it is desirable to add aluminum to themelt phase manufacture early, such as before the polycondensation zone,to provide the benefit of shorter reaction time and/or a highermolecular weight build-up. An aluminum compound is added preferablytogether with reactants at the onset of the esterification reaction orstep A, and prior to entry of the oligomer mixture into thepolycondensation zone or Step (B); or alternatively, no later than whenthe It.V. of the melt reaches 0.3 dL/g, or no later than when the It.V.of the melt reaches 0.2 dL/g.

Once the polymer molecular weight is built to the desired degree, it isdischarged from the final polycondensation reactor, in this case afinisher, to be pelletized. A gear pump may be utilized to facilitatefunneling an amount of bulk polymer through a conduit to exit fromfinishing vessel.

It is to be understood that the melt phase process conditions andreactor configurations described above are illustrative of a melt phaseprocess, and that the invention is not limited to this illustrativeprocess. For example, while reference has been made to a variety ofoperating conditions at certain discrete It.V. values, differing processconditions may be implemented inside or outside of the stated It.V.values, or the stated operating conditions may be applied at It.V.points in the melt other than as stated. Moreover, one may adjust theprocess conditions based on reaction time instead of measuring orpredicting the It.V. of the melt. The process is also not limited to theuse of tank reactors in series or parallel or to the use of differentvessels for each zone.

The melt phase product is processed to a desired form, such as amorphousparticles. The shape of the copolyester polymer particles is notlimited, and can include regular or irregular shaped discrete particleswithout limitation on their dimensions, including stars, spheres,particles, globoids, cylindrically shaped pellets, conventional pellets,pastilles, and any other shape, but particles are distinguished from asheet, film, preforms, strands or fibers.

The method for solidifying the copolyester polymer from the melt phaseprocess is not limited. For example, molten copolyester polymer from themelt phase process may be directed through a die, or merely cut, or bothdirected through a die followed by cutting the molten polymer. A gearpump may be used as the motive force to drive the molten copolyesterpolymer through the die. Instead of using a gear pump, the moltencopolyester polymer may be fed into a single or twin screw extruder andextruded through a die, optionally at a temperature of 190° C. or moreat the extruder nozzle. Once through the die, the copolyester polymercan be drawn into strands, contacted with a cool fluid, and cut intopellets, or the polymer can be pelletized at the die head, optionallyunderwater. The copolyester polymer melt is optionally filtered toremove particulates over a designated size before being cut. Anyconventional hot pelletization or dicing method and apparatus can beused, including but not limited to dicing, strand pelletizing and strand(forced conveyance) pelletizing, pastillators, water ring pelletizers,hot face pelletizers, underwater pelletizers and centrifugedpelletizers.

The particles can be spheroidal in shape by cutting the moltencopolyester underfluid (e.g. underwater) at the die head as the moltenpolymer is extruded through the die head. This process can bedifferentiated form strand cutting operations where the extruded polymeris fed into a water bath, allowed to cool and then the strands are cutafter the polymer is solidified in the strand form.

Articles can be formed from the solid products produced by the processof the invention by any conventional techniques known to those of skill.For example, the melt phase products are fed to a machine for meltextruding and injection molding the melt into shapes such as preformssuitable for stretch blow molding into beverage or food containers, or amachine for injection molding, or a machine for merely extruding intoother forms such as sheet. Suitable processes for forming the articlesare known and include extrusion, extrusion blow molding, melt casting,injection molding, a melt to mold process, stretch blow molding (SBM),thermoforming, and the like.

Examples of the kinds of shaped articles which can be formed from themelt phase products and the copolyester polymer composition of theinvention include sheet; film; packaging and containers such aspreforms, bottles, jars, and trays; rods; tubes; lids; and filaments andfibers. Beverage bottles made from polyethylene terephthalate suitablefor holding water or carbonated beverages, and heat-set beverage bottlessuitable for holding beverages which are hot filled into the bottles areexamples of the types of bottles which are made from the crystallizedpellet of the invention. Examples of trays are those which are dualovenable and other CPET trays. The copolyester polymers can be used invarious types of film and/or sheet, including but not limited toextruded film(s) and/or sheet(s), calendered film(s) and/or sheet(s),compression molded film(s) and/or sheet(s), solution casted film(s)and/or sheet(s). Methods of making film and/or sheet include but are notlimited to extrusion, calendering, compression molding, and solutioncasting.

Copolyester blends comprising the copolyester and a polymer oringredient other than the copolyester can be made. Copolyester blendsmay contain from 0.01 to 25% by weight of the overall composition commonadditives such as colorants, dyes, mold release agents, flameretardants, plasticizers, nucleating agents, stabilizers, including butnot limited to, UV stabilizers, thermal stabilizers and/or reactionproducts thereof, fillers, and impact modifiers. Examples of typicalcommercially available impact modifiers well known in the art and usefulin this invention include, but are not limited to, ethylene/propyleneterpolymers, functionalized polyolefins such as those containing methylacrylate and/or glycidyl methacrylate, styrene-based block copolymericimpact modifiers, and various acrylic core/shell type impact modifiers.Residues of such additives are also contemplated as part of thecopolyester composition

Reinforcing materials may be useful in the polymer blends of thisinvention. The reinforcing materials may include, but are not limitedto, carbon filaments, silicates, mica, clay, talc, titanium dioxide,Wollastonite, glass flakes, glass beads and fibers, and polymeric fibersand combinations thereof. In one embodiment, the reinforcing materialsinclude glass, such as, fibrous glass filaments, mixtures of glass andtalc, glass and mica, and glass and polymeric fibers.

The copolyesters of the invention are desirably thermally stable. Theweight average molecular weight (Mw) of a dry copolyester is measuredbefore melting and then again after remelting to determine its thermalstability. Desirably, the copolyesters of the invention are thermallystable, meaning that the weight average molecular weight (Mw) of thecopolyesters of the invention after heating in a nitrogen atmosphere at310° C. and holding the sample molten for 25 minutes is 15,000 or higheras determined by the GPC method described below. The Mw averagemolecular weight can be at least 17,000, or at least 18,000, or at least19,000, or at least 20,000, or at least 21,000.

For the purpose of determining whether the copolyester is thermallystable, the following test method may be employed. Approximately 200 mgof dried polymer granules with a particle size of 3 mm or less areplaced in a dry GC headspace vial. A screw type cap with a septa insertis firmly attached to the vial to insure a good seal. The contents arepurged with nitrogen by first piercing the septa with an open 18 gaugehypodermic needle that served as an exhaust. A second 18 gauge needleattached to an open nitrogen line with an adapter and Tygon tubing isinserted through the septum. Purging is performed for one minute toprovide an inert atmosphere. A total of 6 vials/experiment are preparedin this manner. The vials are then placed in a heating block at 310° C.and extracted after 0, 5, 10, 15, 20 and 25 minutes. After cooling toroom temperature, the samples are submitted for Gel PermeationChromatography (GPC) where their molecular weight distribution ismeasured. GPC is performed on an Agilent Series 1200 series LCinstrument consisting of a degasser, an isocratic pump, an auto samplerand a UV detector. Each sample is dissolved in a solvent system made upof 95/5 by volume methylene chloride/hexafluoroisopropanol+0.5 g/Ltetraethylammonium bromide. Samples are analyzed under the followingconditions:

-   -   Temperature: ambient    -   Flow rate: 1.0 ml/min    -   Sample solution: 6 mg NPG/TMCD copolyester in 10 ml methylene        chloride/hexafluoroisopropanol azeotrope (˜70/30 by vol)+10 μl        toluene flow rate marker.    -   Injection volume: 10 μl    -   Column set: Polymer Laboratories 5 μm PLgel, Guard+Mixed C    -   Detection: UV absorbance at 255 nm    -   Calibrants: monodisperse polystyrene standards, MW=580 to        4,000,000 and 1-phenyl-Hexane MW=162    -   Universal calibration parameters:        -   Polystyrene PS K=0.1278 a=0.7089        -   Polycyclohexylene dimethylene terephthalate PCT K=0.23568            a=0.8405        -   (Note) The universal calibration parameters above are            determined by linear regression to yield the correct weight            average molecular weights for a set of five PCT samples            previously characterized by light scattering.

Using the above described method, a molecular weight loss (MWL) can alsobe calculated and is determined by the difference between the startingaverage molecular weight (Mw) before exposure (t=0) and the Mw after 25minutes at 310° C. From this, a % MWL is calculated for eachcopolyester.

The amorphous copolyester composition is capable of having a molecularweight loss of less than 25% as determined by measuring the molecularweight difference between a dried (at 80 C for at least 24 hours)polymer having a molecular weight measured at ambient conditions beforea first melting and the molecular weight of the same polymer sampleafter melting it for 25 minutes at a temperature of 310° C. in anitrogen atmosphere. The MWL can be as low as no more than 20%, or nomore than 18%, or no more than 15%, or no more than 13%, or no more than11%, or no more than 10%, or no more than 9%, or no more than 8%.

The copolyesters of the invention desirably also have good meltviscosity stability reported as a melt viscosity loss (“MVL”) of lessthan 50%, or less than 35%, or no more than 30%, or no more than 25%.The melt viscosity stability is also another measure of thermalstability. The melt stability of copolyesters can be determined bymeasuring the melt viscosity loss at a constant temperature and shearrate over a fixed period of time. Desirably, the copolyesters of thisinvention have a melt viscosity of 1,000 Poise or greater when tested ona Rheometrics Dynamic Analyzer (RDAII) at a constant temperature of 300°C. with a 10% strain at a constant frequency of 25 rad/sec after 20minutes in air. Prior to testing, the polymer is ground to a particlesize of 3 mm or less and then dried under vacuum at a temperature closeto its glass transition temperature (Tg) for a minimum of 16 hours. Themelt viscosity (Poise) of a sample with an approximate weight of 2 gramsis measured at 0 and after 20 minutes under the above conditions. The %melt viscosity loss (MVL) is calculated from the 0 and 20 minute data.

The copolyesters of the invention desirably have a low off-gas rate.Desirably, the copolyesters have an off-gas rate of 2.5 ug/g/min orless, or 1.5 μg/g/min or less, or less than 1.25 μg/g/min, or less than1.10 μg/g/min, or less than 1.00 μg/g/min, or less than 0.90 μg/g/min,or less than 0.80 μg/g/min, or less than 0.70 μg/g/min, or less than0.60 μg/g/min, when tested using a sample weight of 2 grams under thefollowing test conditions.

The method is a capillary gas chromatographic procedure for thedetermination of the rate of CO and CO₂ off-gassing produced by heatingcopolyesters. With this method, a known amount of dried copolyester issealed in a headspace GC vial, purged under nitrogen and heated. The gasabove the sealed sample is analyzed by an external standard method usinga dual channel gas chromatograph.

The lab apparatus for this testing procedure consists of the following:

-   -   Dual channel Micro GC    -   Headspace sampler    -   Chromatography data system    -   Module with thermal conductivity detector and        divinylbenzene/ethylene glycol dimethylacryalte capillary        column, 8-m×320-μm id with film thickness=30 μm    -   Module with thermal conductivity detector and 5 Å molecular        sieve zeolite capillary column, 10-m×320-μm id with film        thickness=12 μm    -   Oven for drying samples    -   Vials, 20-mL, headspace, screw-top    -   Septum caps, headspace, screw-top    -   17.5-mm PTFE-Silicone Septa    -   Teflon Tape    -   B-D 21G1 needle    -   Hose with needle attachment connected to nitrogen source

Prior to testing, the copolyester is dried at 60° C. for a minimum of 2hours. Approximately 2.00 grams (±0.02) grams of dried sample are placedin a dry 20-mL headspace vial. The sample weight is recorded to thenearest 0.0001 grams Teflon tape is wrapped around the threaded top ofthe vial to which a screw top cap containing a 17.5 mm PTFE-siliconeseptum if securely attached. Another section of Teflon tape is thenwrapped around the cap and top of vial. The septum is pierced first witha 21 gauge needle to serve as a vent and then with a second needleattached to a hose and nitrogen source. The nitrogen flow is turned onlow and the vial is purged with nitrogen for 3-5 minutes. Afterwards,the vent needle is removed first and then the needle attached to thenitrogen flow. Purged sample vials are then placed in an auto samplertray where they are transferred and inserted into a heating block at300° C. As the sample is heated, the gas above the molten polymer issampled 19 times over a one hour and 5 minute period. The ppm CO and CO₂are calculated for each sample using the data system software oroptionally by the following equation.

${{ppm}\mspace{14mu}{of}\mspace{14mu}{sample}\mspace{14mu}{component}} = \frac{{Area}\mspace{14mu}{of}\mspace{14mu}{sample}\mspace{14mu}{component}\mspace{14mu}{peak} \times {RF}\mspace{14mu}{of}\mspace{14mu}{sample}\mspace{14mu}{component}}{2\mspace{14mu}{grams}\mspace{14mu}\left( {{Sample}\mspace{14mu}{Weight}} \right)}$

The data are used to determine an off gas rate as ppm/min. Prior tosample analysis, a three point calibration at 1000, 5000, and 10000 ppmof CO and CO₂ is performed using known standards of each gas.Integration of the chromatograms and the concentrations of each gas areused to calculate a response factor for each sample component using thefollowing equation.

${{RF}\mspace{14mu}{of}\mspace{14mu}{Sample}\mspace{14mu}{Component}} = {\frac{{Concentration}\mspace{14mu}{of}\mspace{14mu}{Sample}\mspace{14mu}{Component}}{{Area}\mspace{14mu}{of}\mspace{14mu}{Sample}\mspace{14mu}{Component}}\begin{matrix}\left( {{for}\mspace{14mu}{each}\mspace{14mu}{level}} \right) \\\left( {{for}\mspace{14mu}{each}\mspace{14mu}{level}} \right)\end{matrix}}$

The three response factors for each sample component are then averaged.

INSTRUMENT CONDITIONS Channel A Injection Options Inject Time: 100 msecPost Run Time: 0 sec Sample Pump Type: Timed Sample Pump Interval: 30sec Backflush Time: 7 sec Temperature Control Options Sample Inlet: Onat 100 deg C. Injector: On at 90 deg C. Column: On at 100 deg C.Pressure Control Options Pressure Control: On Equilibration Time: 0 secColumn: 32.00 psi (Carrier Gas: Helium) Post Run: 32.00 psi DetectorOptions Filament On: On Autozero: On Sensitivity: High AcquisitionChannel: On Sampling Frequency: 20 Hz Run Time: 2 min Acquisition Delay:0 min Channel B Injection Options Inject Time: 100 msec Post Run Time: 0sec Backflush Time: 10 sec Temperature Control Options Injector: On at90 deg C. Column: On at 90 deg C. Pressure Control Options PressureControl: On Equilibration Time: 0 sec Column: 30.00 psi Post Run: 30.00psi Detector Options Filament On: On Autozero: On Sensitivity: HighAcquisition Channel: On Sampling Frequency: 20 Hz Run Time: 2 minAcquisition Delay: 0 min Trigger Type External (for first injection) Nottriggered (for remaining 18 injections)

Headspace Conditions

HEADSPACE CONDITIONS Cycle HS-Inj Syringe 5.0 mL-HS Sample Volume 3.6 mLIncubat Temp OFF Incubat Time 00:00:04 Agi Speed 500 rpm Agi On Time 0 sAgi Off Time 0 s Syringe Temp OFF Fill Speed 1 mL/s Pullup Del 0 msInject to GC Inj 1 Inject Speed 920 nL/s Pre Inj Del 0 ms Pst Inj Del 0ms Syr Flushing 00:00:00 GC Runtime 00:01:00

EXAMPLES

All polymerizations were conducted on a 0.40 mole scale using a Camile™interfaced polymerization stand. In each case the desired amount of DMT,NPG and TMCD were added to a 500 ml polymerization flask. The flask wasequipped with a nitrogen inlet and stainless steel stirrer. The contentswere purged under nitrogen and then heated in a metal bath under anitrogen sweep of 0.5 SCFH to sweep over the methanol byproduct duringthe ester exchange phase (EE) of the polymerization. In some cases, a 40wt % TMCD methanol solution was used as starting material. In theseinstances, the polymerization flask was barely dipped in the heatedmetal bath until most of the charged methanol distilled over which tookapproximately 10 minutes. Afterwards, the flask was lowered until themolten metal covered the flask approximately ½ in. above the melt levelin the flask. After the EE phase was complete, the flask was completelysubmerged in the metal bath. Vacuum was then applied to the system inorder to build molecular weight. As the molecular weight/melt viscosityof the polymer increased in the finisher stage, the stirring speed wasreduced to maintain good heat contact and surface renewal of the polymermelt.

Examples 1-18 High Temperature Preparation of NPG-TMCD Copolyesters

This method will be referred to as the high temperature preparationmethod. The material charges for the first successful run are asfollows:

Charge to 500 Ml Round Bottom Flask

-   -   Dimethyl terephthalate (0.40 mole)=77.7 g    -   Neopentyl glycol (0.30 mole)=31.3 g    -   2,2,4,4-tetramethylcyclobutanediol (0.30 mole)=43.3 g    -   Butyltin tris-2-ethylhexanoate, lithium hydroxide monohydrate,        aluminum isopropoxide and triphenyl phosphate were added to give        the amounts reported in Table 2.

The process conditions for the high temperature preparation method arereported in Table 1:

TABLE 1 Polymerization Conditions for High Temperature Prep Time TempVac. Stir stage (min.) (° C.) (torr) (rpm) 1 5 200 730 0 2 10 200 730200 3 45 200 730 200 4 5 210 730 200 5 55 210 730 200 6 60 290 730 200 720 290 730 200 8 20 290 0.3 200 9 240 290 0.3 200 10 1 290 730 0 461 or7.7 hr

The above method was used for the initial successful runs. In somecases, slight variations in the hold times and/or prepolymertemperatures and/or the stirring speed were instituted, but the finishertemperature (290° C.) and time (240 minutes) shown in stage 9 were heldconstant.

Table 2 documents the analytical results of copolymers prepared usingthe high temperature preparation method with supporting examples 1-18.

TABLE 2 NPG-TMCD Copolyesters from High Temperature Prep (FinisherTemperature = 290° C., Finisher Time = 4 hours) TMCD meas. in polymermeas. in polymer 2nd meas. in polymer Ex. Batch It. V. mole % % heat Tg(ppm) no. no. (dL/g) NPG TMCD c-TMCD t-TMCD (° C.) Sn P Li Al 1 A 0.390NDA NDA NDA NDA NDA  50-c  6-c 0 0 2 A 0.338 55.2 44.6 51.5 48.5 NDA100-c  12-c 0 0 3 A 0.782 65.9 32.8 60.5 39.5 103 63 8 43 38 4 A 0.74257.6 40.2 60.0 40.0 111 66 7 42 34 5 A 0.731 49.8 48.7 59.6 40.4 121 557 40 35 6 A 0.666 59.3 39.7 60.3 39.7 111 63 11 22 49 7 A 0.748 59.439.4 61.2 38.9 112 57 4 31 24 8 C 0.711 59.1 39.3 77.0 23.0 114 31 4 3148 9 B 0.648 62.5 36.0 73.4 26.7 108 37 3 26 51 10 D 0.744 62.8 35.570.0 30.0 108 31 3 27 53 11 D 0.226 67.3 32.6 69.8 30.2 NDA  30-c  3-c 25-c 0 12 D 0.394 59.3 40.4 62.3 37.7 NDA  35-c  4-c 0  35-c 13 D 0.69066.7 31.6 70.5 29.5 102 0 0 32 57 14 D 0.693 62.6 36.1 70.4 29.6 108 314 31 53 15 D 0.687 78.9 18.2 66.7 33.3 89 34 3 27 39 16 D 0.571 25.372.8 66.3 33.8 156 32 5 27 50 17 D 0.668 60.3 36.4 NDA NDA NDA 33 4 2638 18 D 0.840 63.9 34.7 69.7 30.0 107 13 0 32 59 NDA = No Data Availablec = charged levels of catalysts, not measured.

Table 2 illustrates many points of interest. Examples 3-10 and 13-18show that a high temperature process in combination with an effectivecatalyst system (Sn/Li/Al/P, Sn, /Li/Al, Li/Al) can be used to producehigh IV copolyesters containing TMCD and NPG with a broad range of glasstransition temperatures (Tg). Examples 3-7, 8-10, and 13-18 show thatTMCD batches (A-D) containing different ratios of cis/trans isomers (%)can be used (A=42/58, B=58/42 C&D=53/47). Examples 1 and 2 show that aSn/P catalyst system alone does not produce high IV polymer and thatincreasing Sn concentration appears to actually lower the IV. Examples11 and 12 show that Sn/P in combination with either Li or Al alone doesnot produce high IV polymer. Example 13 and 18 show that high IV polymercan be obtained with Li/Al catalysts alone or in combination with low Sn(13 ppm). The addition of Sn catalyst increases TMCD incorporation.

Examples 19-45 Low Temperature Preparation of NPG-TMCD Copolyesters

Copolyesters were also prepared using a low temperature preparationmethod, which employed a lower finisher temperature (280° C.) and inmost cases, less finisher time (3 hours). Some of the notabledifferences instituted during the low temperature prep were: more Sncatalyst, the addition of Zn or Ti cocatalysts, the elimination of P,lower glycol/acid mole ratio (MR) and longer hold times during esterexchange. The addition points of Li/Al, and Zn and Ti cocatalysts werevaried from up front to the midpoint of stage 3. The advantage of thelow temperature prep is to increase TMCD yield by lowering TMCD excessand lessening the amount of TMCD lost due to chain end degradation. Thetrans isomer of TMCD degrades at elevated temperatures via anelimination reaction, which has the effect of enriching the cis TMCDisomer content in the finished copolyester.

The material charges for a typical low temperature prep are as follows:

Charge to 500 Ml Round Bottom Flask

-   -   Dimethyl terephthalate or T (0.40 mole)=77.7 g    -   Neopentyl glycol or 11 (0.32 mole)=32.9 g    -   ˜40 wt % TMCD in methanol=83.4 g (33.4 g or 0.23 mole of TMCD)    -   Butyltin tris-2-ethylhexanoate, lithium hydroxide monohydrate,        aluminum isopropoxide, zinc acetate and titanium        tetraisopropoxide were added to give the amounts of catalyst        metals measured in the finished polymers reported in Table 4.

The process conditions and reaction sequence for the low temperaturepreparation method are reported in Table 3

TABLE 3 Polymerization Conditions for Low Temperature Prep Stage TimeTemp. Vacuum Stir no (min) (° C.) (torr) rpm 1 0.1 200 730 150 2 15 205730 150 3 120 205 730 150 4 15 230 730 150 5 60 230 730 150 6 15 260 250150 7 30 260 250 150 8 10 270 3.5 150 9 50 270 3.5 150 10 5 275 0.8 15011 45 275 0.8 150 12 5 280 0.8 150 13 240 280 0.8 150 14 3 290 730 0613.1 min or 10.2 hr

The same basic polymerization techniques were used for both the low andhigh temperature prep methods.

Table 4 documents the analytical results of copolymers prepared usingthe low temperature preparation method with supporting examples 19-45.

TABLE 4 NPG-TMCD Copolyesters from Low Temperature Prep (FinisherTemperature = 280° C.) Finisher meas. In polymer meas. In polymer meas.in polymer Ex. time It. V. (mole %) (%) (ppm) no. (hr) (dL/g) NPG TMCDc-TMCD t-TMCD Sn Li Al Zn Ti 19 3 0.683 67.5 30.9 61.8 38.2 0 35 51 0 020 3 0.670 68.4 29.6 62.6 37.4 0 31 59 0 5 21 4 0.620 62.4 32.5 62.437.6 0 24 37 77 0 22 4 0.665 64.0 34.8 60.7 39.3 47 24 35 0 0 23 4 0.62862.6 36.4 59.6 40.5 75 21 40 0 0 24 4 0.575 60.7 38.4 56.8 43.2 155 2232 0 0 25 3.5 0.707 56.6 41.7 58.3 41.7 67 28-l 42-l 0 0 26 3 0.681 56.142.1 57.8 42.2 70 29-l 44-l 0 0 27 3.5 0.701 56.4 41.8 58.3 41.7 71 2845 0 0 28 3.5 0.743 56.8 41.6 58.0 42.0 56 29-l 27-l 0 0 29 3.5 0.73155.9 42.6 57.7 42.3 56 29 19 0 0 30 3.5 0.788 56.2 42.3 57.9 42.1 5531-l 42-l 0 0 31 3.5 0.704 56.0 42.9 57.6 42.4 53 20-l 30-l 0 0 32 3.50.716 55.5 43.4 57.1 42.9 71 19-l 22-l 0 0 33 3.5 0.650 59.6 39.0 60.939.1 50 19-l 24-l 0 0 34 3.5 0.740 58.0 40.6 57.8 42.2 57 21-l 28-l 0 035 3.5 0.738 57.6 41.0 57.7 42.4 58 21-l 25-l 0 0 36 3.5 0.692 58.1 40.458.1 41.9 55 20-l 27-l 0 0 37 3 0.704 62.0 36.1 59.4 40.6 56 34-l 53-l 00 38 3 0.701 62.4 36.3 59.8 40.2 59 30-l 44-l 41-l 0 39 3 0.711 60.837.4 58.8 41.2 60 34-l 50-l 37-l 0 40 3 0.674 60.9 37.4 58.9 41.1 5332-l 27-l 41-l 0 41 3 0.657 60.1 38.2 58.5 41.5 36 27-l 50-l 41 0 42 3.50.768 56.9 41.4 58.0 42.0 58 23-l 27-l 0 5 43 3.5 0.722 58.3 40.4 58.341.7 60 23-l 27-l 0 10-l 44 3.5 0.462 58.0 41.6 55.9 44.1 58 0 0 0  9-l45 3.5 0.433 58.3 41.0 55.6 44.4 54 0 0 0 13-l l = late additions (after60 minutes at 205° C.)

Examples (19-21) in Table 4 show that acceptably high IV copolymercontaining NPG and TMCD can be prepared with Li/Al, Li/Al/Ti andLi/Al/Zn catalyst combinations. Examples 19, 22, 23 & 24 were preparedusing the same charges of NPG and TMCD to show the effect of Sn catalystconcentration on TMCD incorporation. Higher Sn resulted in more TMCDincorporation, but lower IV. High catalyst loadings of Sn alone or Snwith Li/Al added up front to the paste appeared to cause foaming, whichis undesirable. Examples 25-43 show that adding Sn up front, followed bylater additions of Li/Al, Li/Al/Zn or Li/Al/Ti help increase IV, reducefinisher time and lessen the chance of foaming. Examples 44 and 45 showthat a catalyst combination of Sn/Ti alone does not produce high IVpolymer.

Examples 46-49 NPG-TMCD Copolyesters Containing CHDM

Copolyesters of DMT, NPG and TMCD were also prepared containing1,4-cyclohexanedimethanol (CHDM). A low temperature preparation methodin combination with Sn, Li, Al catalysts were used to successfullyprepare copolyesters with 3-11 mole % CHDM. The material charges for atypical run containing low CHDM are shown below along withpolymerization conditions in Table 5.

Charge to 500 Ml Round Bottom Flask

-   -   Dimethyl terephthalate or T (0.40 mole)=77.7 g    -   Neopentyl glycol or 11 (0.28 mole)=29.2 g    -   ˜40 wt % TMCD in methanol=79.3 g (31.7 g or 0.22 mole of TMCD)    -   1,4-cyclohexanedimethanol (0.014 mole)=2.00 g    -   Butyltin tris-2-ethylhexanoate, lithium hydroxide monohydrate        and aluminum isopropoxide were added to give the amounts of        catalyst metals measured in the finished polymers reported in        Table 6.

TABLE 5 Synthesis Procedure for NPG-TMCD Copolymers with CHDM Stage TimeTemp Vacuum Stir no. (min.) (° C.) (torr.) (rpm) 1 0.1 205 730 0 2 15205 730 150 3 120 205 730 150 4 15 230 730 150 5 60 230 730 150 6 15 260250 150 7 30 260 250 150 8 10 270 3.5 150 9 50 270 3.5 150 10 5 275 0.8150 11 45 275 0.8 150 12 5 280 0.8 150 13 90 280 0.8 150 14 1 280 0.8100 15 14 280 0.8 100 16 1 280 0.8 50 17 34 280 0.8 50 18 1 280 0.8 2519 24 280 0.8 25 20 1 280 0.8 10 21 44 280 0.8 10 22 3 290 730 0 583.1min or 9.72 hr

Table 6 documents the analytical results of NPG-TMCD copolymers preparedcontaining CHDM with supporting examples 46-49.

TABLE 6 NPG-TMCD Copolyesters with CHDM Finisher calculated meas. inpolymer Ex. Temp It.V. (mole %) 2nd heat Tg (ppm) no. (° C.) (dL/g) NPG*TMCD* CHDM* (° C) Sn P Li Al 46 280-290 0.676 54.9 34.0 11.7 105 49 4 3025 47 280 0.706 56.5 39.9 3.4 109 56 0 20-l 27-l 48 280 0.737 54.8 38.16.7 109 50 0 23-l 25-l 49 280 0.724 52.6 38.0 10.4 109 50 0 22-l 28-l l= late addition (added after 60 minutes in stage 3 of the polymerizationconditions shown in Table 5). *calculated values based on wt %measurement by gas chromatography. Accurate measurements of CHDM and NPGcould not be determined by NMR due to peak overlap. All compositionsthat did not contain CHDM were determined by NMR.

Examples 50-53 TMCD Degradation

Table 7 shows the effect of finisher temperature and time on TMCDdegradation. The starting cis/trans isomer ratio (%) of the incomingTMCD monomer was 53/47 (cis/trans). As can be seen by examples 50 and51, the cis/trans ratio for finished polymers using the high temperatureprep method was about 70/30. The high cis content is due to degradationof the trans isomer via an elimination reaction (which is a pathway notavailable to the cis isomer due to steric constraints). A highercis/trans ratio in the finished polymer compared to that of the startingmonomer is an indication of the undesired degradation of thetrans-isomer to non-reactive byproducts. Examples 52 and 53 showcopolyesters prepared using the low temperature prep method. Thecis/trans ratio in these copolyesters was 60/40, indicating lesstrans-TMCD degradation.

TABLE 7 The Effect of Finisher Temperature on TMCD Chain End Degradation(Finisher Time = 4 hours) meas. meas. in meas. Fin- in polymer in isherpolymer (%) polymer Ex. Temp. It. V. (mole %) c- t- (ppm) no. (° C.)(dL/g) NPG TMCD TMCD TMCD Sn P Li Al 50 290 0.744 62.8 35.5 70.0 30.0 313 27 53 51 290 0.693 62.6 36.1 70.4 29.6 31 4 31 53 52 280 0.628 62.636.4 59.6 40.4 75 0 21 40 53 280 0.665 64.0 34.8 60.7 39.3 47 0 24 35

Examples 54-60 Scale Up Experiments

NPG/TMCD copolyesters were prepared in a pilot plant using a 30-lb batchstyle reactor (Unit HV). The batches required very long finisher timesto obtain acceptable It.V's of >0.556 dL/g or greater for testing. Thethermal stability and off gassing behavior were evaluated in the samemanner as that described for the lab prep materials. The procedures forsuccessful pilot plant runs are described below. Table 8 reports thebatch analytical data.

Example 54

21.24 lbs dimethyl terephthalate, 10.25 lbs neopentyl glycol and 8.52lbs 2,2,4,4-tetramethyl-1,3-cyclobutanediol were reacted together in thepresence of butyltin tris(2-ethylhexanoate), triphenyl phosphate,lithium hydroxide monohydrate and aluminum isopropoxide to give theamounts of catalyst metals measured in the finished polymers reported inTable 8. The catalysts were charged in a 50/50 mixture of ethyleneglycol/neopentyl glycol with approximate concentrations of 0.20 wt % Sn,0.21 wt % Al, 0.15 wt % Li and 0.015 wt % P. The reaction was carriedout under a nitrogen gas purge of 10 SCFH in an 18 gallon stainlesssteel pressure vessel fitted with a condensing column, a vacuum system,and a HELICONE-type agitator. The contents were heated to 50° C. and theagitator was started at 25 rpm in the forward direction. Heating andstirring were continued for 2.25 hrs until the reaction temperature was290° C. The temperature was held at 290° C. for 30 minutes with theagitator operating at 25 rpm for 6 minutes in the forward direction and6 minutes in the reverse direction. The pressure was then reduced at arate of 13 mm Hg/minute to full vacuum. When the pressure dropped below3.6 mm Hg, the mixture was stirred at 25 rpm for 1 hr and then slowed to15 rpm. The reaction continued at 290° C. at a pressure between 1.4mm-0.90 mm Hg for 8 hours. Upon completion, the vessel was pressurizedwith N₂ to push the molten polymer through an extrusion die. The moltenrods were pulled through a cold water bath to solidify them and choppedinto ˜⅛-inch pellets.

Example 55

23.47 lbs dimethyl terephthalate, 9.81 lbs neopentyl glycol and 12.19lbs 2,2,4,4-tetramethyl-1,3-cyclobutanediol were reacted together in thepresence of butyltin tris(2-ethylhexanoate), triphenyl phosphate,lithium hydroxide monohydrate and aluminum isopropoxide to give theamounts of catalyst metals measured in the finished polymers reported inTable 8. The catalysts were charged in a 50/50 mixture of ethyleneglycol/neopentyl glycol with approximate concentrations of 0.20 wt % Sn,0.20 wt % Al, 0.15 wt % Li and 0.014 wt % P. The reaction was carriedout under a nitrogen gas purge of 10 SCFH in an 18 gallon stainlesssteel pressure vessel fitted with a condensing column, a vacuum system,and a HELICONE-type agitator. The contents were heated to 50° C. and theagitator was started at 25 rpm in the forward direction. Heating andstirring were continued for 1.33 hrs until the reaction temperature was290° C. The temperature was held at 290° C. for 30 minutes with theagitator operating at 25 rpm for 6 minutes in the forward direction and6 minutes in the reverse direction. The pressure was then reduced at arate of 13 mm Hg/minute to full vacuum. When the pressure dropped below2.5 mm Hg, the reaction proceeded at 25 rpm until the power draw to theagitator no longer increased (˜8 hr). The pressure range during the 8hour finisher time was 2.5 mm to 0.83 mm Hg. Upon completion, the vesselwas pressurized with N₂ to push the molten polymer through an extrusiondie. The molten rods were pulled through a cold water bath to solidifythem and chopped into ˜⅛-inch pellets.

Example 56

23.47 lbs dimethyl terephthalate, 8.18 lbs neopentyl glycol and 13.41lbs 2,2,4,4-tetramethyl-1,3-cyclobutanediol were reacted together in thepresence of butyltin tris(2-ethylhexanoate), triphenyl phosphate,lithium hydroxide monohydrate and aluminum isopropoxide to give theamounts of catalyst metals measured in the finished polymers reported inTable 8. The catalysts were charged in a 50/50 mixture of ethyleneglycol/neopentyl glycol with approximate concentrations of 0.20 wt % Sn,0.20 wt % Al, 0.15 wt % Li and 0.014 wt % P. The reaction was carriedout under a nitrogen gas purge of 10 SCFH in an 18 gallon stainlesssteel pressure vessel fitted with a condensing column, a vacuum system,and a HELICONE-type agitator. The contents were heated to 50° C. and theagitator was started at 25 rpm in the forward direction. Heating andstirring were continued to 205° C. where the contents were held for 1hour. The temperature was then increased to 290° C. and held for 30minutes with the agitator operating at 25 rpm for 6 minutes in theforward direction and 6 minutes in the reverse direction. Afterwards,the pressure was reduced at a rate of 13 mm Hg/minute to full vacuum.When the pressure dropped below 3.9 mm Hg, wattmeter readings wereobserved until the power draw to the agitator no longer increased (˜7.5hr). At this time, the stir speed was reduced to 10 rpm and the reactionproceeded at 290° C. for 2 additional hours. The pressure range duringthe 9.5 hour finisher time was 3.9 mm to 0.79 mm Hg. Upon completion,the vessel was pressurized with N₂ to push the molten polymer through anextrusion die. The molten rods were pulled through a cold water bath tosolidify them and chopped into ˜⅛-inch pellets.

Example 57

23.47 lbs dimethyl terephthalate, 9.00 lbs neopentyl glycol and 10.60lbs 2,2,4,4-tetramethyl-1,3-cyclobutanediol were reacted together in thepresence of butyltin tris(2-ethylhexanoate) to give the amount of Snmeasured in the finished polymer reported in Table 8. The reaction wascarried out under a nitrogen gas purge of 10 SCFH in an 18 gallonstainless steel pressure vessel fitted with a condensing column, avacuum system, and a HELICONE-type agitator. The contents were heated to50° C. and the agitator was started at 25 rpm in the forward direction.Heating and stirring were continued to 205° C. where the contents wereheld for 1 hour. Afterwards, lithium hydroxide monohydrate and aluminumisopropoxide were added to give the amounts of Li and Al measured in thefinished polymer reported in table 8. The Li and Al were added throughthe main catalyst charge port in a 50/50 mixture of ethylene glycol andneopentyl glycol with approximate concentrations of 0.16 wt % Li and0.21 wt % Al. The catalyst charge port was then rinsed with n-butanol toensure complete transfer of the catalysts. The reaction mixture was heldfor an additional hour at 205° C. and then heated to 230° C. and heldfor an hour. When the 230° C. hold time was complete, the mixture washeated to 260° C. and held for 0.5 hour with the agitator operating at25 rpm for 6 minutes in the forward direction and 6 minutes in thereverse direction. Afterwards, the pressure was reduced at a rate of 13mm Hg/minute to full vacuum while heating to 280° C. When thetemperature reached 280° C. and the pressure dropped below 3.3 mm Hg,the mixture was stirred at 25 rpm for 9 hours. At this time, the powerto the agitator appeared to peak so the stir speed was reduced to 15 rpmand the reaction continued for one hour. The pressure range during the10 hour finisher time was 3.3 mm to 0.27 mm Hg. Upon completion, thevessel was pressurized with N₂ to push the molten polymer through anextrusion die. The molten rods were pulled through a cold water bath tosolidify them and chopped into ˜⅛-inch pellets.

Example 58

23.47 lbs dimethyl terephthalate, 9.00 lbs neopentyl glycol, 10.60 lbs2,2,4,4-tetramethyl-1,3-cyclobutanediol and 0.50 lbs of1,4-cyclohexanedimethanol were reacted together in the presence ofbutyltin tris(2-ethylhexanoate) to give the amount of Sn measured in thefinished polymer reported in Table 8. The reaction was carried out undera nitrogen gas purge of 10 SCFH in an 18 gallon stainless steel pressurevessel fitted with a condensing column, a vacuum system, and aHELICONE-type agitator. The contents were heated to 50° C. and theagitator was started at 25 rpm in the forward direction. Heating andstirring were continued to 205° C. where the contents were held for 1hour. Afterwards, lithium hydroxide monohydrate and aluminumisopropoxide were added to give the amounts of Li and Al measured in thefinished polymer reported in table 8. The Li and Al were added throughthe main catalyst charge port in a 50/50 mixture of ethylene glycol andneopentyl glycol with approximate concentrations of 0.16 wt % Li and0.21 wt % Al. The catalyst charge port was then rinsed with n-butanol toensure complete transfer of the catalysts. The reaction mixture was heldfor an additional hour at 205° C. and then heated to 230° C. and heldfor an hour. When the 230° C. hold time was complete, the mixture washeated to 260° C. and held for 0.5 hour with the agitator operating at25 rpm for 6 minutes in the forward direction and 6 minutes in thereverse direction. Afterwards, the pressure was reduced at a rate of 13mm Hg/minute to full vacuum while heating to 280° C. When thetemperature reached 280° C. and the pressure dropped below 2.7 mm Hg,the mixture was stirred at 25 rpm for 9 hours. The pressure range duringthe 9 hour finisher time was 2.7 mm to 0.26 mm Hg. Upon completion, thevessel was pressurized with N₂ to push the molten polymer through anextrusion die. The molten rods were pulled through a cold water bath tosolidify them and chopped into ˜⅛-inch pellets.

Example 59

23.47 lbs dimethyl terephthalate, 9.00 lbs neopentyl glycol, 10.60 lbs2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1.00 lbs of1,4-cyclohexanedimethanol were reacted together in the presence butyltintris(2-ethylhexanoate) to give the amount of Sn measured in the finishedpolymer reported in Table 8. The reaction was carried out under anitrogen gas purge of 10 SCFH in an 18 gallon stainless steel pressurevessel fitted with a condensing column, a vacuum system, and aHELICONE-type agitator. The contents were heated to 50° C. and theagitator was started at 25 rpm in the forward direction. Heating andstirring were continued to 205° C. where the contents were held for 1hour. Afterwards, lithium hydroxide monohydrate and aluminumisopropoxide were added to give the amounts of Li and Al measured in thefinished polymer reported in table 8. The Li and Al were added throughthe main catalyst charge port in ethylene glycol with approximateconcentrations of 0.32 wt % Li and 0.37 wt % Al. The catalyst chargeport was then rinsed with n-butanol to ensure complete transfer of thecatalysts. The reaction mixture was held for an additional hour at 205°C. and then heated to 230° C. and held for an hour. When the 230° C.hold time was complete, the mixture was heated to 260° C. and held for0.5 hour with the agitator operating at 25 rpm for 6 minutes in theforward direction and 6 minutes in the reverse direction. Afterwards,the pressure was reduced at a rate of 13 mm Hg/minute to full vacuumwhile heating to 280° C. When the temperature reached 280° C. and thepressure dropped below 2.1 mm Hg, the mixture was stirred at 25 rpm for9 hours. The pressure range during the 9 hour finisher time was 2.1 mmto 0.44 mm Hg. Upon completion, the vessel was pressurized with N₂ topush the molten polymer through an extrusion die. The molten rods werepulled through a cold water bath to solidify them and chopped into˜⅛-inch pellets.

Example 60

23.47 lbs dimethyl terephthalate, 9.00 lbs neopentyl glycol, and 10.60lbs 2,2,4,4-tetramethyl-1,3-cyclobutanediol were reacted together in thepresence of butyltin tris(2-ethylhexanoate) to give the amount of Snmeasured in the finished polymer reported in Table 8. The reaction wascarried out under a nitrogen gas purge of 10 SCFH in an 18 gallonstainless steel pressure vessel fitted with a condensing column, avacuum system, and a HELICONE-type agitator. The contents were heated to50° C. and the agitator was started at 25 rpm in the forward direction.Heating and stirring were continued to 205° C. where the contents wereheld for 1 hour. Afterwards, lithium hydroxide monohydrate and aluminumisopropoxide were added to give the amounts of Li and Al measured in thefinished polymer reported in table 8. The Li and Al were added throughthe main catalyst charge port in ethylene glycol with approximateconcentrations of 0.32 wt % Li and 0.37 wt % Al. The catalyst chargeport was then rinsed with n-butanol to ensure complete transfer of thecatalysts. The reaction mixture was held for an additional hour at 205°C. and then heated to 230° C. and held for an hour. When the 230° C.hold time was complete, the mixture was heated to 260° C. and held for0.5 hour with the agitator operating at 25 rpm for 6 minutes in theforward direction and 6 minutes in the reverse direction. Afterwards,the pressure was reduced at a rate of 13 mm Hg/minute to full vacuumwhile heating to 280° C. When the temperature reached 280° C. and thepressure dropped below 4 mm Hg, the mixture was stirred at 25 rpm for 9hours. The pressure range during the 9 hour finisher time was 4 mm to0.17 mm Hg. Upon completion, the vessel was pressurized with N₂ to pushthe molten polymer through an extrusion die. The molten rods were pulledthrough a cold water bath to solidify them and chopped into ˜⅛-inchpellets.

Table 8 documents the analytical results of NPG-TMCD copolyestersprepared in batch unit HV of the research Pilot Plant with supportingpatent examples 54-60.

TABLE 8 Pilot Plant Batch Analytical Data Finisher Finisher meas. inpolymer 2nd meas. In polymer Ex. Temp Time It.V. (mole %) heat Tg (ppm)no. (° C.) (hr) (dL/g) NPG TMCD CHDM (° C.) Sn P Li Al 54 290 7.92 0.64472.8 25.8 0.00 95 42 3 29 40 55 290 8.13 0.611 65.1 33.4 0.00 102 34 226 40 56 290 9.48 0.579 57.1 41.2 0.00 108 36 2 25 35 57 280 10.00 0.70258.50 40.2 0.00 106 45 0 27-l 30-l 58 280 9.00 0.673 *57.0 *37.6 *2.70106 42 0 27-l 36-l 59 280 9.00 0.610 *49.4 *41.8 *5.37 112 32 0 25-l30-l 60 280 9.00 0.668 57.3 41.1 0.000 110 51 0 24-l 31-l -l = lateaddition - (after holding at 205° C. for one hour. For more detail, seepilot plant procedures above.) *calculated values based on wt %measurements by gas chromatography. Accurate measurements of CHDM andNPG could not be determined by NMR due to peak overlap. All compositionsthat did not contain CHDM were determined by NMR. Note: all batchescontained small amount of ethylene glycol (<2 mole %) from the catalystsolution.

Examples 61-91 Thermal Stability

Table 9 documents the molecular weight loss of NPG-TMCD and CHDM-TMCDcopolyesters after 25 minutes at 310° C. in a nitrogen atmosphere withpatent examples 61-91.

TABLE 9 Molecular Weight at 310° C. at Time 0 and 25 Minutes meas. inpolymer 310 C. 310 C. Ex. Prep meas. in polymer ppm Mw Mw 310 C. no.type NPG TMCD CHDM Sn P Li Al Ti Zn t = 0 t = 25 MWL 61 Lab 67.5 30.90.0 0 0 35 51 0 0 22257 18972 3285 62 Lab 68.4 29.6 0.0 0 0 31 59 5 022049 17231 4818 63 Lab 63.0 37.0 0.0 0 0 72 58 26 0 22197 15453 6744 64Lab 70.0 26.4 0.0 0 0 31-l 42-l 33 0 26839 19538 7301 65 Lab 65.2 33.40.0 11 0 32 62 0 0 24346 22302 2044 66 Lab 63.9 34.7 0.0 13 0 32 59 0 030166 26919 3247 67 Lab 25.3 72.8 0.0 32 5 27 50 0 0 17697 16850 847 68Lab 62.6 35.8 0.0 33 9? 27 49 0 0 21110 19625 1485 69 PP 65.1 33.4 0.034 2 26 40 0 0 19489 17841 1648 70 PP 57.1 41.2 0.0 36 2 25 35 0 0 1809116218 1873 71 PP 72.8 25.8 0.0 42 3 29 40 0 0 20992 19372 1620 72 PP58.5 40.2 0.0 45 0 27-l 30-l 0 0 22634 19580 3054 73 PP 57.3 41.1 0.0 510 24-l 31-l 0 0 21317 18806 2511 74 Lab 49.8 48.7 0.0 55 7 40 35 0 023723 19010 4713 75 Lab 57.6 41.0 0.0 58 0 21-l 25-l 0 0 24272 182196053 76 Lab 65.9 32.8 0.0 63 8 43 38 0 0 25970 20031 5939 77 Lab 59.339.7 0.0 63 11 22 49 0 0 21445 18755 2690 78 Lab 57.6 40.2 0.0 66 7 4234 0 0 23970 20333 3637 79 Lab 56.9 41.4 0.0 58 0 23-l 27-l  5-l 0 2551219359 6153 80 Lab 58.3 40.4 0.0 60 0 23-l 27-l 10-l 0 23688 18073 561581 Lab 60.9 37.4 0.0 53 0 32-l 27-l 0 41-l 22268 18245 4023 82 Lab 56.5*39.9* 3.4* 56 0 20 27 0 0 23359 19544 3815 83 PP 53.2* 39.7* 4.0* 37 026-l 33-l 0 0 19925 17361 2564 84 Lab 54.8* 38.1* 6.7* 50 0 23 25 0 024099 19093 5006 85 Lab 52.6* 38.0* 10.4* 50 0 22 28 0 0 23386 184954891 86 Lab 54.9* 34.0* 11.7* 49 4 30 25 0 0 21144 17970 3174 87 Lab 0.034.6 62.4 58 6 20-l 19-l 0 0 17497 12674 4823 88 Lab 0.0 33.3 65.8 67 920 56 0 0 18451 13079 5372 89 PP 0.0 21.4 75.9 194 14 0 0 0 0 1905713218 5839 90 prod. 0.0 21.5 78.5 183 12 0 0 0 0 20825 13653 7172 91prod. 0.0 35.0 65.0 168 11 0 0 0 0 18644 13382 5262 t = time in minutesPP = Pilot Plant Material Prod. = Production Material l = late addition(after 60 minutes at 205° C.) *calculated levels based on GC wt %measurements MWL = molecular weight loss (initial − final)

Examples 61-81 show that copolyesters containing NPG and TMCD maintain aweight average molecular weight (Mw) of 15,000 or greater after 25minutes at 310° C. when prepared with catalyst systems of Li/Al,Sn/Li/Al, and optionally containing P, Ti and Zn. Examples 82-86 showthat a Mw above 15,000 can also be maintained after 25 minutes at 310°C. if CHDM is added to NPG-TMCD copolyesters at up to 12 mole %.Examples 87 and 88 show that a Mw less than 15,000 after 25 minutes at310° C. resulted when CHDM-TMCD copolyesters were prepared using aSn/Li/Al/P catalyst system. Examples 89-91 show that a Mw of less than15,000 after 25 minutes at 310° C. also resulted when production andpilot plant samples of CHDM-TMCD (prepared with high levels of Sncatalyst) were tested.

Examples 92-116 Off Gassing Performance

Off gassing can be a problem during high temperature film extrusion ofCHDM-TMCD copolyesters. This behavior is thought to be caused byvolatile degradation components attributed to CHDM and TMCD degradationand often results in splay defects in the sheet

The off-gas results for NPG-TMCD copolyesters compared to CHDM-TMCDcopolyesters are shown in Table 10 with patent examples 92-116.

TABLE 10 Off Gas Rates of NPG-TMCD copolyesters Finisher meas. in Polmermeas. In Polymer measured Ex. Prep Temp (mole %) (ppm) off gas (μ/g/min)no. Type (° C.) NPG TMCD CHDM Sn P Li Al Ti Zn CO CO₂ rate 92 lab 29065.9 32.8 0.0 63 8 43 38 0 0 0.155 0.280 0.435 93 lab 290 57.6 40.2 0.066 7 42 34 0 0 0.595-a 0.376-a 0.971-a 94 lab 290 49.8 48.7 0.0 55 7 4035 0 0 0.477-a 0.337-a 0.814-a 95 lab 290 59.3 39.7 0.0 63 11 22 49 0 00.343 0.527 0.869 96 lab 290 59.4 39.4 0.0 57 4 31 24 0 0 0.252 0.4610.659 97 PP 290 72.8 25.8 0.0 42 3 29 40 0 0 0.599 0.343 0.941 98 PP 29065.1 33.4 0.0 34 2 26 40 0 0 0.416 0.352 0.768 99 PP 290 57.1 41.2 0.036 2 25 35 0 0 0.315 0.342 0.657 100 lab 280 57.6 41.0 0.0 58 0 21-l25-l 0 0 0.994 0.629 1.623 101 lab 280 62.0 36.1 0.0 56 0 34-l 53-l 0 01.075 0.546 1.620 102 PP 280 58.5 40.2 0.0 45 0 27 30 0 0 0.696 0.7891.486 103 PP 280 57.3 41.1 0.0 51 0 24 31 0 0 0.464 0.664 1.128 104 lab280 62.4 36.3 0.0 59 0 30-l 44-l 0 41-l 1.681 0.659 2.340 105 lab 28060.8 37.4 0.0 60 0 34-l 50-l 0 37-l 1.308 0.616 1.924 106 lab 280 60.937.4 0.0 53 0 32-l 27-l 0 41-l 1.139 0.565 1.704 107 lab 280 56.9 41.40.0 58 0 23-l 27-l  5-l 0 0.992 0.593 1.585 108 lab 280 58.3 40.4 0.0 600 23-l 27-l 10-l 0 0.997 0.672 1.669 109 lab 280 56.5* 39.9* 3.4* 56 020 27 0 0 1.033 0.644 1.677 110 lab 280 54.8* 38.1* 6.7* 50 0 23 25 0 01.015 0.697 1.712 111 lab 280 52.6* 38.0* 10.4* 50 0 22 28 0 0 1.0610.848 1.909 112 PP 280 53.2* 39.7* 4.0* 37 0 26 33 0 0 0.650 0.720 1.369113 PP 285 0.0 21.4 0.0 194 14 0 0 0 0 4.707 3.827 8.588 114 lab 290 0.034.6 64.6 58 6 20 19 0 0 0.358 1.402 1.760 115 prod. 282-e 0.0 21.5 78.5183 12 0 0 0 0 1.264-a 2.763-a 4.027-a 116 prod. 282-e 0.0 35.0 65.0 16811 0 0 0 0 1.137-a 2.193-a 3.330-a -e = estimates -l = late addition(after 60 minutes at 205° C.) -a = average of two separate measurementsPP = pilot plant prod. = production samples *= calculated levels basedon GC wt % measurements

Examples 92-99 show that NPG-TMCD copolyesters prepared with theSn/Li/Al/P catalyst system at the highest finisher temperature (290° C.)had the lowest off gas rates. Examples 100-112 show that the off gasrate increased when the finisher temperature was lowered to 280° C.Examples 104-106 show that the addition of Zn cocatalyst at ˜30-50 ppmresulted in slightly higher off gas rates. Examples 107 & 108 where lowlevel Ti cocatalyst (5-10 ppm) was added did not appear to adverselyaffect the off gas rate. The off gas rates of all NPG-TMCD copolyestersprepared with Sn, Li, Al and optionally P, and Zn & Ti, cocatalysts werelower than Tritan™ TX-1000 and TX-2000 controls (Examples 115 & 116)which contain CHDM in place of NPG. Example 113, a Tritan™ TX-1000control prepared in the Pilot Plant had the highest off gas rate.Example 114 shows that a CHDM-TMCD copolyester prepared at a highfinisher temperature (290° C.) using low level Sn, Li, Al & P had a ratethat was considerably lower than the ones prepared with very high Sn incombination with P (Examples 113, 115 & 116).

Examples 117-122 Melt Stability

Melt viscosity loss data are shown in Table 11 with supporting patentexamples 117-122.

TABLE 11 Melt Viscosity loss at 300° C. in air at 25 rad/sec meas. inpolymer meas. in polymer Viscosity (Poise) Ex. It. V. mole % Tg (ppm) 020 no. (dL/g) NPG *TMCD CHDM (° C.) Sn P Li Al min. min. (MVL) 117 0.721 0 21 79 108 194 14 0 0 1230 341 889 118 0.747  0 22 78 108 183 12 0 02230 695 1535 119 0.644 74 26  0 95 42 3 29 40 1560 1203 357 120 0.57959 41  0 108 36 2 25 35 1873 1442 431 121 0.668 59 41  0 110 51 0 25-l30-l 3619 2553 1066 122 0.642  56*  40*  4* 106 37 0 26-l 33-l 2875 1990885 Note: Example 118 = Tritan ™ TX-1000 sample. -l = late addition(after 60 minutes at 205° C.) Examples 117 and 119 - 122 are pilot plantprepared samples. *= calculated levels based on GC wt % measurements

Examples 117 and 118 show that the melt viscosity of 80 mole % CHDM/20mole % TMCD copolyesters dropped to less than 1,000 Poise after 20minutes at 300° C. in air regardless of whether it was a Tritan™production sample (Ex. 118) or pilot plant sample (Ex. 117). Examples119-121 show the melt viscosity of NPG-TMCD copolyesters prepared withSn/Li/Al and optionally P maintained a melt viscosity greater than 1,000Poise under the same conditions. Example 122 shows that a melt viscosityof greater than 1,000 Poise can also be maintained under the sameconditions when low CHDM (4 mole %) is added to an NPG-TMCD copolyester.

What we claim is:
 1. An amorphous copolyester composition comprising: a)residues of 2,2,4,4-tetraalkyl-1,3-cyclobutanediol (TACD); b) residuesof neopentyl glycol (NPG); c) alkali metal atoms or alkaline earth metalatoms; d) aluminum atoms; e) tin atoms; f) an It.V. of at least 0.55dL/g; and g) a Tg of at least 90° C.
 2. The copolyester of claim 1,wherein the copolyester is not solid state polymerized.
 3. Thecopolyester of claim 1, wherein the Tg of the copolyester is at least100° C.
 4. The copolyester of claim 1, wherein the Tg of the copolyesteris at least 105° C.
 5. The copolyester of claim 1, wherein the It.V. ofthe copolyester is at least 0.58 dL/g.
 6. The copolyester of claim 1,wherein the It.V. of the copolyester is at least 0.60 dL/g.
 7. Thecopolyester of claim 1, wherein the It.V. of the copolyester is at least0.67 dL/g.
 8. The copolyester of claim 1, wherein the copolyestercomprises less than 4 mole % residues of hydroxyl modifiers, based onthe moles of all residues in the copolyester.
 9. The copolyester ofclaim 1, wherein the copolyester comprises less than 2 mole % residuesof hydroxyl modifiers, based on the moles of all residues in thecopolyester.
 10. The copolyester of claim 1, wherein no hydroxylmodifiers other than ethylene glycol are added to a melt phase processfor manufacture of the copolyester composition, provided that ifethylene glycol is added to the melt phase process, it is added only asa carrier for one or more of the alakali metals or alkaline earthmetals, aluminum, or tin atoms.
 11. The copolyester of claim 1, whereinthe copolyester comprises less than 1 mole % residues of ethyleneglycol, based on the moles of all residues in the copolyester.
 12. Thecopolyester of claim 1, wherein said TACD residue comprises the residueof a compound represented by the structure:

wherein R₁, R₂, R₃, and R₄ each independently represent an alkyl radicalhaving 1 to 8 carbon atoms.
 13. The copolyester of claim 1, wherein theTACD residue comprises a residue of2,2,4,4-tetramethylcyclobutane-1,3-diol,2,2,4,4-tetraethylcyclobutane-1,3-diol,2,2,4,4-tetra-n-propylcyclobutane-1,3-diol,2,2,4,4-tetra-n-butylcyclobutane-1,3-diol,2,2,4,4-tetra-n-pentylcyclobutane-1,3-diol,2,2,4,4-tetra-n-hexylcyclobutane-1,3-diol,2,2,4,4-tetra-n-heptylcyclobutane-1,3-diol,2,2,4,4-tetra-n-octylcyclobutane-1,3-diol,2,2-dimethyl-4,4-diethylcyclobutane-1,3-diol,2-ethyl-2,4,4-trimethylcyclobutane-1,3-diol,2,4-dimethyl-2,4-diethyl-cyclobutane-1,3-diol,2,4-dimethyl-2,4-di-n-propylcyclobutane-1,3-diol,2,4-n-dibutyl-2,4-diethylcyclobutane-1,3-diol,2,4-dimethyl-2,4-diisobutylcyclobutane-1,3-diol,2,4-diethyl-2,4-diisoamylcyclobutane-1,3-diol, or mixtures thereof. 14.The copolyester of claim 1, wherein the residues of NPG are present inthe copolyester in an amount of at least 7 mole %, based on the moles ofall residues in the copolyester.
 15. The copolyester of claim 1, whereinthe residues of NPG are present in the copolyester in an amount rangingfrom 5 to 20 mole %, based on the moles of all residues in thecopolyester.
 16. The copolyester of claim 1, wherein tin atoms arepresent in the copolyester in an amount of at least 10 ppm based on theweight of the copolyester polymer.
 17. The copolyester of claim 1,further comprising zinc atoms.
 18. The copolyester of claim 1, whereinthe copolyester is made without the addition of a titanium catalyst to amelt phase process for the manufacture of the copolyester.
 19. Thecopolyester of claim 1, wherein the copolyester is made without theaddition of any catalytically active metal or metal compounds other thansaid tin, aluminum, alkali metal or alkaline earth metal atoms, andoptionally zinc.
 20. The copolyester of claim 1, wherein the copolyestercomprises the residues of: (a) an acid component comprising at least 80mole % of the residues of terephthalic acid or residues of derivates ofterephthalic acid; and (b) a hydroxyl component comprising at least 80mole % of the residues of NPG and TACD, cumulative; based on 100 molepercent of acid component residues and 100 mole percent of hydroxylcomponent residues in the copolyester polymer.
 21. The copolyester ofclaim 20, wherein the copolyester comprises residues of: (a) an acidcomponent comprising at least 96 mole % terephthalate units; and (b) ahydroxyl component comprising at least 96 mole residues of TACD and NPG,cumulative; based on 100 mole percent of the acid component residues and100 mole percent of the hydroxyl component residues in the copolyesterpolymer.
 22. The copolyester of claim 1, wherein the TACD residuecomprises a residue of 2,2,4,4-tetramethylcyclobutane-1,3-diol (“TMCD”).23. The copolyester of claim 22, wherein the mole % of residues of TMCDpresent in the copolyester, based on the moles of all residues in thecopolyester, is at least 20 mole %.
 24. The copolyester of claim 22,wherein the mole % of residues of TMCD present in the copolyester, basedon the moles of all residues in the copolyester, is at least 30 mole %.25. The copolyester of claim 1, wherein the copolyester comprises atleast 15 ppm Al atoms, based on the weight of the copolyester.
 26. Thecopolyester of claim 25, comprising at least 30 ppm Al atoms based onthe weight of the copolyester.
 27. The copolyester of claim 1, whereinthe copolyester comprises alkali metal atoms, said alakali metal atomscomprising Li atoms.
 28. The copolyester of claim 27 wherein copolyestercomprises Li atoms present in the copolyester in an amount ranging from10 ppm to 60 ppm, based on the weight of the copolyester.
 29. Thecopolyester of claim 28, wherein the Li atoms are present in an amountranging from 25 ppm to 50 ppm, based on the weight of the copolyester.30. The copolyester of claim 1, wherein said copolyester furthercomprises phosphorus atoms.
 31. The copolyester of claim 30, whereinsaid copolyester comprises phosphorus atoms present in an amount of atleast 1 ppm.
 32. The copolyester of claim 1, wherein said copolyester isthermally stable, defined as having a weight average molecular weight(Mw) of 15,000 or greater if measured by melting a dried sample of thecopolyester (dried at 80° C. for at least 24 hours) in a nitrogenatmosphere at 310° C. and determining the Mw molecular weight of themolten sample by GPC after holding the sample molten for 25 minutes. 33.The copolyester of claim 32, wherein the Mw average molecular weight ofthe copolyester is at least 17,000 or greater.
 34. The copolyester ofclaim 33, wherein said copolyester has the property of having amolecular weight loss of no more than 13% when holding molten for atleast 25 minutes.
 35. The copolyester of claim 34, wherein saidcopolyester has the property of having a molecular weight loss of nomore than 11%.
 36. The copolyester of claim 35, wherein said copolyesterhas the property of having a molecular weight loss of no more than 9%.37. The copolyester of claim 1, wherein the copolyester has an off-gasrate of 2.5 μg/g/min or less.
 38. The copolyester of claim 37, whereinthe off-gas rate is less than 1.5 μg/g/min.
 39. The copolyester of claim37, wherein the off-gas rate is less than 1.25 μg/g/min.
 40. Thecopolyester of claim 1, wherein the copolyester is thermally stable asdetermined by having a melt viscosity loss property of less than 50%.41. The copolyester of claim 40, wherein the melt viscosity loss is lessthan 35%.
 42. The copolyester of claim 40, wherein the melt viscosityloss is no more than 30%.
 43. The copolyester of any one of claims 1-25,wherein tin atoms are present in the copolyester in an amount of atleast 20 ppm and up to 100 ppm, based on the weight of the copolyester.44. A sheet, film, bottle, jar, tray, rod, tube, lid, filament, or fibercomprising the copolyester of claim 1.